25XГT
2025-06-13 09:12:44 Origin： Remark：0 Click：
ГОСT 4543 -1971 Specification for Steel Round bar 25XГT forgings, Plate stock available ESR ingot, Hot blooming / rolling / forging 25XГT Heat treatment
MATERIAL DESIGNATION - 25XГT
Material specifications: ГОСT 4543 -1971
Available in stock: round bar diam. 50 ~ 270mm
PRODUCT DESCRIPTION
The alloy is usually produced by EAF + VD + LF / BEF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - Quenched and tempered.
Rod / round bar / disc (diameter): 5.5 ~ 600mm
Square bar & flat bar: 8 ~ 500mm
Plate & Sheet: cold & hot rolled / forged T 2.0 ~ 300 X W 10 ~ 1000 X L mm
Square bar & flat bar: 8 ~ 500mm
Plate & Sheet: cold & hot rolled / forged T 2.0 ~ 300 X W 10 ~ 1000 X L mm
TYPICAL CHEMICAL ELEMENTS (mass weight %)
Carbon, C (％): 0.22 ~ 0.29
Silicon, Si (％): 0.17 ~ 0.37
Carbon, C (％): 0.22 ~ 0.29
Silicon, Si (％): 0.17 ~ 0.37
Manganese, Mn (％): 0.80 ~ 1.10
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.025
Chromium, Cr (％): 1.00 ~ 1.30
Nickel, Ni (%): ≤ 0.30
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.025
Chromium, Cr (％): 1.00 ~ 1.30
Nickel, Ni (%): ≤ 0.30
Molybdenum, Mo (％): -
Titanium, Ti (%): 0.03 ~ 0.09
Ferrum, Fe (%): remainder.
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT
Heat treatment temperature / ℃, annealing: -
Heat working temperature / ℃: 1200 ~ 900
Heat treatment temperature / ℃, quenching: 880 ~ 950 oil cooling
Heat treatment temperature / ℃, tempering : 200 air / water cooling
Hardness under annealing condition ≤ HBW: 217
Tensile strength, Rm ≥ MPa: 1275
Yield strength, Rp0.2 ≥ MPa: 980
Elongation, A5 ≥ (%): 9.0
Reduction of area, Z ≥ (%): 45.0
Impact strength, AK ≥ J: 59
Hardness after final heat treatment / HBW: -
Hardness under annealing condition ≤ HBW: 217
Tensile strength, Rm ≥ MPa: 1275
Yield strength, Rp0.2 ≥ MPa: 980
Elongation, A5 ≥ (%): 9.0
Reduction of area, Z ≥ (%): 45.0
Impact strength, AK ≥ J: 59
Hardness after final heat treatment / HBW: -
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Steel bar and steel forgings for barrel of middle-small caliber quick firing arms.
Power generation – turbine fasteners – boiler support rods.
Process plant – fasteners, Mechanical gears, gear shaft, main axis, valve rod.
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Steel bar and steel forgings for barrel of middle-small caliber quick firing arms.
Power generation – turbine fasteners – boiler support rods.
Process plant – fasteners, Mechanical gears, gear shaft, main axis, valve rod.
TECHNICAL SALES ASSISTANCE & SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
If you are interested in our products or services, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers or sales department.
Hot search：25XГT
Total list
Monthly rank
- 51AMS 6419
- 1927NiCrMoV11-6
- 1938NCD4
- 17AMS 6418
- 1620C15
- 1626NiCrMoV11-5
- 1624CrMo5
- 1542Cr4Mo2
- 14B5F5B
- 14EN52 & EN 52