20H2M
2026-03-09 15:20:24 Origin： Remark：0 Click：
ГОСT 4543 -1971 Nickel - Molybdenum steel round bar 20H2M heat treated forgings 20H2M flat bar, plate, ESR remelting technique, hot bloomed / rolled / forged, cold drawn rod
TECHNICAL DATA SHEET - 20H2M
Material category: 1.7Ni - 0.2Mo base alloy steel
Technical specifications: ГОСT 4543 -1971
Available from stock: round bar diam. 30 ~ 120 mm
PRODUCT DESCRIPTION
The alloy 20H2M is usually produced by EAF + VD + LF / BEF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Material category: 1.7Ni - 0.2Mo base alloy steel
Technical specifications: ГОСT 4543 -1971
Available from stock: round bar diam. 30 ~ 120 mm
PRODUCT DESCRIPTION
The alloy 20H2M is usually produced by EAF + VD + LF / BEF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - quenched and tempered.
Rod / round bar / disc (diameter): 6.0 ~ 850 mm
Square bar / flat bar: 10 ~ 600 mm
Plate / sheet via cold & hot rolled / forged: THK 0.50 ~ 100 X wdie 20 ~ 1200 X L mm
TYPICAL CHEMICAL ELEMENTS (mass fraction %)
Carbon, C (％): 0.17 ~ 0.25
Silicon, Si (％): 0.17 ~ 0.37
Manganese, Mn (％): 0.40 ~ 0.70
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.025
Chromium, Cr (％): ≤ 0.30
Nickel, Ni (%): 1.50 ~ 1.90
Molybdenum, Mo (％): 0.20 ~ 0.30
Ferrum, Fe (%): balance.
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT
Heat treatment temperature / ℃, annealing: -
Heat working temperature / ℃: 1200 ~ 850
Heat treatment temperature / ℃, quenching: 860 oil cooled
Heat treatment temperature / ℃, tempering: 180 oil / air cooled
Hardness under annealing condition ≤ HBW: -
Tensile strength, Rm ≥ MPa: 883
Yield strength, Rp0.2 ≥ MPa: 686
Elongation, A5 ≥ (%): 10.0
Reduction of area, Z ≥ (%): 50.0
Impact strength, AK ≥ J: 78
Hardness after final heat treatment / HB: -
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Steel bar and steel forgings for barrel of middle-small caliber quick firing arms.
Power generation, turbine fasteners, boiler support rods.
Process plant, fasteners, Mechanical gears, gear shaft, main axis, valve rod.
TECHNICAL SALES ASSISTANCE & SERVICE
20+ years focus on special steel manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
Final heat treatment - quenched and tempered.
Rod / round bar / disc (diameter): 6.0 ~ 850 mm
Square bar / flat bar: 10 ~ 600 mm
Plate / sheet via cold & hot rolled / forged: THK 0.50 ~ 100 X wdie 20 ~ 1200 X L mm
TYPICAL CHEMICAL ELEMENTS (mass fraction %)
Carbon, C (％): 0.17 ~ 0.25
Silicon, Si (％): 0.17 ~ 0.37
Manganese, Mn (％): 0.40 ~ 0.70
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.025
Chromium, Cr (％): ≤ 0.30
Nickel, Ni (%): 1.50 ~ 1.90
Molybdenum, Mo (％): 0.20 ~ 0.30
Ferrum, Fe (%): balance.
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT
Heat treatment temperature / ℃, annealing: -
Heat working temperature / ℃: 1200 ~ 850
Heat treatment temperature / ℃, quenching: 860 oil cooled
Heat treatment temperature / ℃, tempering: 180 oil / air cooled
Hardness under annealing condition ≤ HBW: -
Tensile strength, Rm ≥ MPa: 883
Yield strength, Rp0.2 ≥ MPa: 686
Elongation, A5 ≥ (%): 10.0
Reduction of area, Z ≥ (%): 50.0
Impact strength, AK ≥ J: 78
Hardness after final heat treatment / HB: -
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Steel bar and steel forgings for barrel of middle-small caliber quick firing arms.
Power generation, turbine fasteners, boiler support rods.
Process plant, fasteners, Mechanical gears, gear shaft, main axis, valve rod.
TECHNICAL SALES ASSISTANCE & SERVICE
20+ years focus on special steel manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
Raw material available from stock
Custom 450 / C450 / XM-25 (S45000), 403 ESR, AISI 616 / 422 ESR, B50A365 / 403Cb+
17-4PH / 630, M-152 / 1.4938 / S151, S159, FV520B / S143 / 1.4594. X22CrMoV12-1
13Х11Н2B2MФ / AE961W, 11Х11Н2B2MФ / 16Х11Н2B2MФ
AISI 615 / S41800, 15-5PH / XM-12 (S15500), A-286 AISI 660 / S66286
10705BU, 10705MBU, 10705AJ, S111, S131, S154
Hot search：20H2M
Total list
Monthly rank
- 1738XC
- 13X7NiMo6
- 1334CrNiMo6V
- 1220Mn5Cr5
- 1112CrMo9-10 / 1.7375
- 1038NiCrMoV7-3
- 10AMS 6302
- 1034CrNiMo4
- 9S135
- 9AMS 6320