40XH
2026-03-25 14:15:16 Origin： Remark：0 Click：
ГОСT 4543 -1971 Chromium - Nickel steel round bar heat treated forgings 40XH plate stock available ESR ingot 40XH hot bloomed / rolled / forged, quenched and tempered
TECHNICAL DATA SHEET - 40XH
Material category: 0.6Cr - 1.2Ni - 0.4C base alloy steel
Technical material specifications: ГОСT 4543 -1971
Available from stock: round bar diam. 25 ~ 210 mm
PRODUCT DESCRIPTION
40XH is usually produced by EAF + VD + LF / BEF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Material category: 0.6Cr - 1.2Ni - 0.4C base alloy steel
Technical material specifications: ГОСT 4543 -1971
Available from stock: round bar diam. 25 ~ 210 mm
PRODUCT DESCRIPTION
40XH is usually produced by EAF + VD + LF / BEF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - quenched and tempered.
Rod / round bar / disc (diameter): 6.0 ~ 910 mm
Square bar / flat bar: 8 ~ 620 mm
Plate / sheet via cold & hot rolled / forged: THK 0.50 ~ 200 X wdie 20 ~ 1000 X L mm
TYPICAL CHEMICAL COMPOSITIONS (mass weight %)
Carbon, C (％): 0.36 ~ 0.44
Silicon, Si (％): 0.17 ~ 0.37
Manganese, Mn (％): 0.50 ~ 0.80
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.025
Chromium, Cr (％): 0.45 ~ 0.75
Nickel, Ni (%): 1.00 ~ 1.40
Molybdenum, Mo (％): -
Ferrum, Fe (%): balance.
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT
Heat treatment temperature / ℃, annealing: -
Heat working temperature / ℃: 1150 ~ 850
Heat treatment temperature / ℃, quenching: 820 water or oil cooled
Heat treatment temperature / ℃, tempering: 500 oil / water cooled
Hardness under annealing condition ≤ HB: 217
Tensile strength, Rm ≥ MPa: 980
Yield strength, Rp0.2 ≥ MPa: 785
Elongation, A5 ≥ (%): 11.0
Reduction of area, Z ≥ (%): 45.0
Impact strength, AK ≥ J: 69
Hardness after final heat treatment / HB: -
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Steel bar and steel forgings for barrel of middle-small caliber quick firing arms.
Power generation, turbine fasteners, boiler support rods.
Process plant, fasteners, Mechanical gears, gear shaft, main axis, valve rod.
TECHNICAL SALES ASSISTANCE & SERVICE
20+ years focus on special steel manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
Final heat treatment - quenched and tempered.
Rod / round bar / disc (diameter): 6.0 ~ 910 mm
Square bar / flat bar: 8 ~ 620 mm
Plate / sheet via cold & hot rolled / forged: THK 0.50 ~ 200 X wdie 20 ~ 1000 X L mm
TYPICAL CHEMICAL COMPOSITIONS (mass weight %)
Carbon, C (％): 0.36 ~ 0.44
Silicon, Si (％): 0.17 ~ 0.37
Manganese, Mn (％): 0.50 ~ 0.80
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.025
Chromium, Cr (％): 0.45 ~ 0.75
Nickel, Ni (%): 1.00 ~ 1.40
Molybdenum, Mo (％): -
Ferrum, Fe (%): balance.
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT
Heat treatment temperature / ℃, annealing: -
Heat working temperature / ℃: 1150 ~ 850
Heat treatment temperature / ℃, quenching: 820 water or oil cooled
Heat treatment temperature / ℃, tempering: 500 oil / water cooled
Hardness under annealing condition ≤ HB: 217
Tensile strength, Rm ≥ MPa: 980
Yield strength, Rp0.2 ≥ MPa: 785
Elongation, A5 ≥ (%): 11.0
Reduction of area, Z ≥ (%): 45.0
Impact strength, AK ≥ J: 69
Hardness after final heat treatment / HB: -
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Steel bar and steel forgings for barrel of middle-small caliber quick firing arms.
Power generation, turbine fasteners, boiler support rods.
Process plant, fasteners, Mechanical gears, gear shaft, main axis, valve rod.
TECHNICAL SALES ASSISTANCE & SERVICE
20+ years focus on special steel manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
Raw material available from stock
Custom 450 / C450 / XM-25 (S45000), 403 ESR, AISI 616 / 422 ESR, B50A365 / 403Cb+
17-4PH / 630, M-152 / 1.4938 / S151, S159, FV520B / S143 / 1.4594. X22CrMoV12-1
13Х11Н2B2MФ / AE961W, 11Х11Н2B2MФ / 16Х11Н2B2MФ
AISI 615 / S41800, 15-5PH / XM-12 (S15500), A-286 AISI 660 / S66286
10705BU, 10705MBU, 10705AJ, S111, S131, S154
Hot search：40XH
Previous page：Grade 2 / J12523
Last page：最后一页
Total list
Monthly rank
- 3534CrNiMo6V
- 28AISI/SAE 4063
- 23K14675
- 21EN52 & EN 52
- 2126NiCrMoV11-5
- 1926NiCrMoV14-5
- 1838NiCrMo4
- 16AMS 6304
- 1519CrNi5
- 1518MND5