12Cr2Mo1V
2026-07-24 16:52:38 Origin： Remark：0 Click：
NB/T 47008 - 2017 carbon and alloy steel forgings for pressure equipment 12Cr2Mo1V heat treated round bar, plate 12Cr2Mo1V peeled rod, stock available flat bar
TECHNICAL DATA SHEET - GB 12Cr2Mo1V
Steel type: 2.25Cr - 1.0Mo - 0.03V - 0.12C base alloy steel
Material specifications - NB/T 47008 - 2017
Stock available: plate, flat bar
Profile and dimension available:
Rod & round bar & disc (diameter): 6.0 ~ 900 mm
Square bar & flat bar: 10 ~ 650 mm
Plate & sheet & strip: T 0.5 ~ 300 X W 15 ~ 1000 X L mm
TYPICAL CHEMICAL COMPOSITIONS (mass fraction - %)
Carbon, C (％): ≤ 0.15
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.30 ~ 0.60
Phosphorus, P (％): ≤ 0.020
Sulfur, S (％): ≤ 0.010
Chromium, Cr (％): 2.00 ~ 2.50
Molybdenum, Mo (％): 0.90 ~ 1.10
Nickel, Ni (％): ≤ 0.30
Copper, Cu (%): ≤ 0.20
Vanadium, V (%): 0.25 ~ 0.35
Niobium, Nb (％): ≤ 0.07
Titanium, Ti (％): ≤ 0.030
Phosphorus, P (％): ≤ 0.020
Sulfur, S (％): ≤ 0.010
Chromium, Cr (％): 2.00 ~ 2.50
Molybdenum, Mo (％): 0.90 ~ 1.10
Nickel, Ni (％): ≤ 0.30
Copper, Cu (%): ≤ 0.20
Vanadium, V (%): 0.25 ~ 0.35
Niobium, Nb (％): ≤ 0.07
Titanium, Ti (％): ≤ 0.030
Aluminum, Al (%): -
Nitrogen, N (%): -
Ferrum, Fe (%): remainder.
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT
Heat treatment temperature / ℃ | annealing: -
Heat treatment temperature / ℃ | normalizing: -
Heat treatment temperature / ℃ | quenching: -
Heat treatment temperature / ℃ | tempering : 620
Hardness after annealing, ≤ HB: -
Tensile strength, Rm ≥ MPa: 590 ~ 760
Yield strength, Rp0.2 ≥ MPa: 420
Elongation, A5 ≥ (%): 17.0
Reduction of area, Z ≥ (%): -
Impact strength, AKv ≥ J: 60
Nitrogen, N (%): -
Ferrum, Fe (%): remainder.
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT
Heat treatment temperature / ℃ | annealing: -
Heat treatment temperature / ℃ | normalizing: -
Heat treatment temperature / ℃ | quenching: -
Heat treatment temperature / ℃ | tempering : 620
Hardness after annealing, ≤ HB: -
Tensile strength, Rm ≥ MPa: 590 ~ 760
Yield strength, Rp0.2 ≥ MPa: 420
Elongation, A5 ≥ (%): 17.0
Reduction of area, Z ≥ (%): -
Impact strength, AKv ≥ J: 60
Hardness after final heat treatment / HBW: -
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Mechanical parts - connecting rod, bolt and nuts.
Multi-diameter shaft, pressure vessel parts.
Power generation – turbine fasteners – boiler support rods.
Process plant – fasteners, mechanical gears, gear shaft, main axis, valve rod.
PRODUCT DESCRIPTION
12Cr2Mo1V is usually produced by EAF + VD + LF / BEF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied black in the annealed condition.
Final heat treatment - normalized + tempered
TECHNICAL SALES ASSISTANCE & SERVICE
20+ years focus on special steel manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
We closely cooperate with the professional inspection partners to strictly control the quality and improve the quality manage system, and guarantee the goods delivery each time. It is proved that we are worth of trusting and will be the strategic partner of the supplying chains in the special steels field.
If you are interested in our products or services, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers or sales department.
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Mechanical parts - connecting rod, bolt and nuts.
Multi-diameter shaft, pressure vessel parts.
Power generation – turbine fasteners – boiler support rods.
Process plant – fasteners, mechanical gears, gear shaft, main axis, valve rod.
PRODUCT DESCRIPTION
12Cr2Mo1V is usually produced by EAF + VD + LF / BEF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied black in the annealed condition.
Final heat treatment - normalized + tempered
TECHNICAL SALES ASSISTANCE & SERVICE
20+ years focus on special steel manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
We closely cooperate with the professional inspection partners to strictly control the quality and improve the quality manage system, and guarantee the goods delivery each time. It is proved that we are worth of trusting and will be the strategic partner of the supplying chains in the special steels field.
If you are interested in our products or services, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers or sales department.
Hot search：12Cr2Mo1V
Total list
Monthly rank
- 10918CrNiMo7
- 55A182 Grade F11 Class 2
- 26S154
- 25AISI / SAE 3145
- 22AISI/SAE 6140
- 2130NiCrMo12
- 2150CrVA
- 17X46Cr13
- 16EN 355
- 1534CrNiMo4