Barrel steel PCrNi3Mo
2026-08-30 08:31:13 Origin： Remark：0 Click：
GJB 5207 Specification for alloy steel forgings of cannon barrel parts PCrNi3Mo round bar, plate, ESR remelting process PCrNi3Mo hot forged, rolled, annealed or quenched and tempered
TECHNICAL DATA SHEET - PCrNi3Mo
Technical specification: GJB 5207 - 2003
Key usage: 100 mm barrel gun body, gun breech, 152 mm cannon barrel bodyStock available: round bar, hollow bar, forging block
SHAPES AND DIMENSIONS
Rod, round bar, disc (diameter): 10 ~ 500 mm
Square bar, flat bar: 10 ~ 600 mm
Forging: T20 ~ 600 X W 50 ~ 800 X L mm
TYPICAL CHEMICAL ELEMENTS (mass weight - %)
Carbon, C (％): 0.32 ~ 0.42
Silicon, Si (％): 0.17 ~ 0.37
Manganese, Mn (％): 0.25 ~ 0.50
Phosphorus, P (％): ≤ 0.025
Sulfur, S (％): ≤ 0.020
Chromium, Cr (％): 0.80 ~ 1.20
Nickel, Ni (％): 2.75~ 3.25
Molybdenum, Mo (％): 0.20 ~ 0.30
Vanadium, V (%): -
Ferrum, Fe (%): balance.MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT
Heat treatment temperature / ℃ | annealing: -.
Heat treatment temperature / ℃ | normalizing:
Heat treatment temperature / ℃ | quenching: 880
Heat treatment temperature / ℃ | tempering : 510
Hardness after annealing, ≤ HB: -
Limit of proportionality: 540 / 590 Mpa
Elongation, A5 ≥ (%): 35.0Impact strength, AKv ≥ J: 17
Limit of proportionality: 635 / 685 / 735 / 785 Mpa
Elongation, A5 ≥ (%): 30.0Impact strength, AKv ≥ J: 15
Limit of proportionality: 835 / 885 / 930 Mpa
Elongation, A5 ≥ (%): 25.0Impact strength, AKv ≥ J: 15
Hardness after final heat treatment / HB: -
PRODUCT DESCRIPTION
PCrNi3Mo is usually produced by EAF + VD + LF / BEF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied black in the annealed condition.
Final heat treatment - normalized + quenched + tempered.
TECHNICAL SALES ASSISTANCE & SERVICE
20+ years focus on special steel manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
If you are interested in our products or services, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers or sales department.
PRODUCT DESCRIPTION
PCrNi3Mo is usually produced by EAF + VD + LF / BEF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied black in the annealed condition.
Final heat treatment - normalized + quenched + tempered.
TECHNICAL SALES ASSISTANCE & SERVICE
20+ years focus on special steel manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
If you are interested in our products or services, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers or sales department.
Further, please also check the materials in stock available:
Raw material - steels of blade for steam turbine
XM-25, S45000, GD450, C450
403 ESR, GB8732 type 12Cr12Mo, 10705BA/BB/BC
AISI 616, 422, 1.4935, X20CrMoWV12-1, 10705BU
B50A365B, 403Cb+, 1.4913, X19CrMoVNbN11-1
17-4PH, 630, 1.4542, X5CrNiCuNb16-4, 10705GU/GV/GW
M-152, S64152, 1.4938, X12CrNiMoV12-3, S151D
FV520B, S143, 1.4594, X4CrNiCuMo14-5
X22CrMoV12-1, 1.4923
13Х11Н2B2MФ, AE961W
15-5PH, XM-12, S15500
A286, AISI 660, S66286
10705MBU, 10705AJ
NONMAGNETIC ALLOY STEEL:
1.3813, X40MnCrN19, 1.3816, X8MnCrN18-18
1.3817, X40MnCr18, 1.3818, X55MnCrN18-4
Hot search：
Previous page：Martensitic steel MT 410
Last page：最后一页