1.6932
2014-10-30 15:39:18 Origin： Remark：0 Click：
Material Speficiation DIN EN 10083-2 Hardened Alloy Steel 1.6932 Round bar, 1.6932 Inventory, Stock Available, hot forging, hot rolling, heat treatment
MATERIAL DATA SHEET - Grade W-Nr 1.6932
Inventory and Ex-stock details - bright peeled bar, diam.15 ~ 70mm
Material Category - hardened and tempered steel
Melting process - BEF + ESR
Material Specifications - DIN EN 10083-2 (2006), DIN 17200 (1987)
Material Specifications - DIN EN 10083-2 (2006), DIN 17200 (1987)
Chemical composition (mass weight - %)
Carbon, C (％): 0.24 ~ 0.32
Silicon, Si (％): ≤ 0.40
Manganese, Mn (％): 0.15 ~ 0.40
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 1.00 ~ 1.50
Molybdenum, Mo (％): 0.35 ~ 0.55
Nickel, Ni (％): 1.80 ~ 2.10
Vanadium, V (％): 0.05 ~ 0.15
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESSSilicon, Si (％): ≤ 0.40
Manganese, Mn (％): 0.15 ~ 0.40
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 1.00 ~ 1.50
Molybdenum, Mo (％): 0.35 ~ 0.55
Nickel, Ni (％): 1.80 ~ 2.10
Vanadium, V (％): 0.05 ~ 0.15
Hot working temperature /℃: 1050～850
Heat treatment temperature /℃| annealing: 650～700
Heat treatment temperature /℃| annealing: 650～700
Heat treatment temperature /℃| Normalizing: 850～880
Heat treatment temperature /℃| Quenching: -
Heat treatment temperature /℃| Tempering : -
Hardness after annealing ≤HBS: 248
Heat treatment temperature /℃| Quenching: -
Heat treatment temperature /℃| Tempering : -
Hardness after annealing ≤HBS: 248
Steel dimension /mm: 101 - 160
Tensile Strength, |σb≥/MPa: 800 ~ 950
Yield strength, |σs≥/MPa: 630
Elongation, |δ5≥/(%): 14.0
Reduction of area, |ψ≥/(%): -
Impact, |AKV≥/J: 45
Tensile Strength, |σb≥/MPa: 800 ~ 950
Yield strength, |σs≥/MPa: 630
Elongation, |δ5≥/(%): 14.0
Reduction of area, |ψ≥/(%): -
Impact, |AKV≥/J: 45
PRODUCT DESCRIPTION
The alloy is usually produced by EAF or BEF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - heat treatment / Quenched and tempered.
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Mechanical gears, gear shaft, main axis, valve rod.
Mechanical parts - connecting rod, bolt and nut, Multidiameter shaft.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to email or call our resident team of qualified production engineers. E-mail sales@ccsteels.com
Hot search：1.6932
Previous page：28NiCrMoV8-5
Last page：33NiCrMoV14-5
Total list
Monthly rank
- 3421CrMoV5-11
- 3134CrNiMo6V
- 3016NC6
- 2726NiCrMoV14-5
- 2720NCD2
- 25AISI/SAE 6140
- 23B5F5B
- 2134CrNiMo4
- 2123MnB4 / 1.5535
- 2018MND5