Description 32CrMo12 Round bar, flat bar, plate and forgings. 1.7361 material made from steelmaking, hot forging, hot rolling, heat treated, cold worked.
MATERIAL DATA SHEET - DIN 32CrMo12 & W-Nr 1.7361
MATERIAL CATEGORY - hardened and tempered steel
PRODUCT DESCRIPTION
Alloy structural steel is provided with higher yield strength, tensile strength, endurance strength, yield ratio (about 0.85 generally ) enough plasticity and toughness.
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - heat treatment / QT
MATERIAL SPECIFICATIONS - DIN EN 10083-2 (2006), DIN 17200 (1987)
CHEMICAL COMPOSITION (Mass weight %)
C (％): 0.28 ~ 0.35
Si (％): ≤ 0.40
Mn (％): 0.40 ~ 0.70
P (％)≤: 0.035
S (％)≤: 0.035
Cr (％): 2.80 ~ 3.30
Mo (％): 0.30 ~ 0.50
Ni (％): ≤ 0.60
Si (％): ≤ 0.40
Mn (％): 0.40 ~ 0.70
P (％)≤: 0.035
S (％)≤: 0.035
Cr (％): 2.80 ~ 3.30
Mo (％): 0.30 ~ 0.50
Ni (％): ≤ 0.60
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working temperature /℃: 1100～900
Heat treatment temperature /℃| annealing: 680～720
Heat treatment temperature /℃| annealing: 680～720
Heat treatment temperature /℃| Normalizing: 880～920
Heat treatment temperature /℃| Quenching: 860~900oil
Heat treatment temperature /℃| Tempering : 540~680
Hardness after annealing ≤HBS: 248
Heat treatment temperature /℃| Quenching: 860~900oil
Heat treatment temperature /℃| Tempering : 540~680
Hardness after annealing ≤HBS: 248
Steel dimension /mm: ≤16
TS, |σb≥/MPa: 1230 ~ 1420
YS, |σs≥/MPa: 1030
EL, |δ5≥/(%): 9
RA, |ψ≥/(%): 35
Impact, |AKV≥/J: 34
TS, |σb≥/MPa: 1230 ~ 1420
YS, |σs≥/MPa: 1030
EL, |δ5≥/(%): 9
RA, |ψ≥/(%): 35
Impact, |AKV≥/J: 34
Steel dimension /mm: 17 - 40
|σb≥/MPa: 1230 ~ 14200
|σs≥/MPa: 1030
|δ5≥/(%): 9.0
|σb≥/MPa: 1230 ~ 14200
|σs≥/MPa: 1030
|δ5≥/(%): 9.0
|ψ≥/(%): 35
|AKV≥/J: 34
|AKV≥/J: 34
Steel dimension /mm: 41 - 100
|σb≥/MPa: 1080 ~ 1270
|σs≥/MPa: 885
|δ5≥/(%): 10
|ψ≥/(%): 40
|AKV≥/J: 41
|σb≥/MPa: 1080 ~ 1270
|σs≥/MPa: 885
|δ5≥/(%): 10
|ψ≥/(%): 40
|AKV≥/J: 41
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 1500mm
Plate / Steel strip: 0.1mm to 1500mm
Width: 8mm to 2500mm
Steel sheet: thickness 0.50 ~ 6.00mm, width 1000mm X length 1000/2000mm - Standard size
Length: random length or based on the customer's special requirement
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Mechanical gears, gear shaft, main axis, valve rod.
Mechanical parts - connecting rod, bolt and nut, Multidiameter shaft, Pressure vessel.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to email or call our resident team of qualified production engineers. E-mail: sales@ccsteels.com
Hot search：32CrMo12
Total list
Monthly rank
- 3421CrMoV5-11
- 3134CrNiMo6V
- 3016NC6
- 2726NiCrMoV14-5
- 2720NCD2
- 25AISI/SAE 6140
- 23B5F5B
- 2134CrNiMo4
- 2123MnB4 / 1.5535
- 2018MND5