1.4980
2014-09-15 11:42:44 Origin： Remark：0 Click：
Specifications 1.4980 Inventory Round bars Datasheet, Properties 1.4980 Forging Stock Technical Specifications Melting, ESR & VAR technique, Hot blooming, Hot forging & Rolling, Heat treatment, Straightening, Ultrasonic flaw detection test.
TECHNICAL DATA SHEET - W-Nr. 1.4980
MATERIAL CATEGORY - High temperature high strength steel and superalloy
MATERIAL SPECIFICATIONS - DIN 17742, 17460, 17480, DIN EN 103021, 10296, 10095
AVAILABLE SHAPES
Round bar / flat bar / plate / forgings
Bright - peeled + polishing /centerless grinding /peeled + slidabrading
Forged - ring /pipe casing /discs /shaft
INVENTORY & STOCKLIST - Round bar Diam.20 ~ 140mm
CHEMICAL COMPOSITION ( Mass Weight % )
C (％): 0.03 ~ 0.08
Si (％): ≤ 1.00
Mn (％): 1.00 ~ 2.00
P (％)≤: 0.025
S (％)≤: 0.015
Cr (％): 13.5 ~ 16.0
Ni (％): 24.0 ~ 27.0
Mo (％): 1.00 ~ 1.50
Other (％): Al ≤ 0.35, Ti 1.90 ~ 2.30, V 0.10 ~ 0.50, B 0.003 ~ 0.010
Si (％): ≤ 1.00
Mn (％): 1.00 ~ 2.00
P (％)≤: 0.025
S (％)≤: 0.015
Cr (％): 13.5 ~ 16.0
Ni (％): 24.0 ~ 27.0
Mo (％): 1.00 ~ 1.50
Other (％): Al ≤ 0.35, Ti 1.90 ~ 2.30, V 0.10 ~ 0.50, B 0.003 ~ 0.010
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot forming temperature /℃: 1100～950
Heat treatment temperature /℃ | annealing: -
Heat treatment temperature /℃ | quenching or solution: 885~ 915 water/air
Heat treatment temperature /℃ | tempering: 700~735
Heat treatment temperature /℃ | ageing: 710~730
Condition: precipitation hardening
Mechanical property under room temperature |σb/MPa: 930~1180
Mechanical property under room temperature |σs≥/MPa: 635
Mechanical property under room temperature |σs≥/MPa: 635
Mechanical property under room temperature |δ5≥(％): 12
Mechanical property under room temperature |Akv(DVM): 27
Heat stability temperature/℃: 700
Non-scale temperature in air /℃: 820
MECHANICAL PROPERTY UNDER HIGH TEMPERATURE
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|200: 559
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|300: 539
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|400: 520
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|500: 500
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|600: 451
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|700: 314
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|800: 78
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|300: 539
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|400: 520
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|500: 500
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|600: 451
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|700: 314
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|800: 78
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|600: 441
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|700: 206
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|600: 304
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|700: 118
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|600: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|700: 206
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|600: 304
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|700: 118
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|600: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|700: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|900: -
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 550mm
Plate / Sheet steel / Steel strip: 0.1mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VIM VOD followed by electroslag refining (ESR) or VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the solution annealing condition.
Final heat treatment - heat treatment / QT / solution treatment
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
Gas turbine
Turbine blade, Fuel nozzle, Heat treating fixture.
Furnace muffle, Nuclear reactor, Turbine engine parts - mechanical gears, gear shaft, main axis, blade.
Turbine blade, Fuel nozzle, Heat treating fixture.
Furnace muffle, Nuclear reactor, Turbine engine parts - mechanical gears, gear shaft, main axis, blade.
Mechanical parts - bolt and nut, fastener.
Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.
These materials must stand up to high heat, extreme oxidation potential and recycling.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to email or call our resident team of qualified production engineers. Email: sales@ccsteels.com
Hot search：1.4980
Previous page：X5NiCrTi26-15
Last page：1.4944
Total list
Monthly rank
- 50FSX-414
- 16Aquamet 22
- 1510705BU
- 15AMS 5221
- 13Carpenter 20 Mo 4
- 12X12CrNiMoV12-2
- 11Inconel 610
- 10AMS 5354
- 9Incoloy 840
- 8Aquamet 17