FSX-414
2017-11-11 08:36:01 Origin： Remark：0 Click：
Specification FSX-414 round bar, flat bar plate FSX-414 ESR melted, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold machined.
TECHNICAL DATA SHEET - Grade FSX-414
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Cr - Ni - Co - W alloy
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): 0.20 ~ 0.30
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％)≤: 0.035
Carbon, C (％): 0.20 ~ 0.30
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％)≤: 0.035
Sulfur, S (％)≤: 0.015
Chromium, Cr (％): 27.0 ~ 31.0
Chromium, Cr (％): 27.0 ~ 31.0
Nickel, Ni (％): 9.50 ~ 11.0
Molybdenum, Mo (％): -
Cobalt, Co (%): ≤ 48.7
Cobalt, Co (%): ≤ 48.7
Tungsten, W (%): 6.00 ~ 8.00
Aluminum, Al (%): -
Aluminum, Al (%): -
Copper, Cu (%): -
Titanium, Ti (%): -
Titanium, Ti (%): -
Ferrum, Fe (%): ≤ 2.00
Boron, B (%): ≤ 0.012
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged or Double aged
FORMS & DIMENSIONS
Round bar & Disc (diameter): 5.5 ~ 450mm
Square bar / Flat bar: 10 ~ 450mm
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged or Double aged
FORMS & DIMENSIONS
Round bar & Disc (diameter): 5.5 ~ 450mm
Square bar / Flat bar: 10 ~ 450mm
Wire rod (Diameter): 0.10 ~ 16mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our qualified production engineers.
If you meet further on any technical enquiry, pleased to EMAIL our qualified production engineers.
- Email: sales@ccsteels.com.
Hot search：FSX-414
Previous page：Z3CMN17-07Az
Last page：Z3CN18-07Az