10705BU
2019-05-22 16:47:01 Origin： Remark：0 Click：
Specifications 10705BU datasheet, 10705BU Chemical, 10705BU Ring forging, Bar, 10705BU Wire rod, 10705BU Sheet - steelmaking, ESR, Blooming,616 Forging, Rolling, Heat treat, Straightened, 100% Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing. Material specifications: ASTM A565 or by Agreement.
TURBINE BLADE TECHNICAL DATASHEET - Grade 10705BU
Official test certification: issued by TUV - SGS - BV
MATERIAL CATEGORY - High temperature martensitic chromium bars and forge piece
MATERIAL SPECIFICATIONS - 10705BU & Ref. ASTM A565
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.18 ~ 0.27
Si (％): ≤ 0.55
Mn (％): 0.50 ~ 1.00
P (％)≤: 0.030
S (％)≤: 0.015
Cr (％): 10.85 ~ 12.65
Ni (％): 0.47 ~ 1.03
Mo (％): 0.85 ~ 1.30
W (％): 0.55 ~ 1.30
V (%): 0.17 ~ 0.33
MECHANICAL PROPERTIES UNDER DIFFERENT HEAT TREATED CONDITIONS
Form: bar, flat bar, forge piece
Condition: +A, annealed
Tensile strength σb/MPa: -
Yield strength σ0.2/MPa: -
Elongation δ(％): -
Reduction of area ф(％): -
Hardness | HRB: ≤ 248
Form: bar, flat bar, forge piece
Condition: +HT, tempering (620℃)
Tensile strength σb/MPa: 930
Yield strength σ0.2/MPa: 760
Elongation δ(％): 14.0
Reduction of area ф(％): 32.0
Hardness | HRB: 277 ~ 331
Form: bar,forge piece
Condition: + H, tempering (675℃)
Tensile strength σb/MPa: 825
Yield strength σ0.2/MPa: 585
Elongation δ(％): 17.0
Reduction of area ф(％): 35.
Hardness | HRB: 241~285
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / AOD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered
PRODUCT FORMS & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W70 - 1000mm X L1000-12000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com,
MATERIAL CATEGORY - High temperature martensitic chromium bars and forge piece
MATERIAL SPECIFICATIONS - 10705BU & Ref. ASTM A565
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.18 ~ 0.27
Si (％): ≤ 0.55
Mn (％): 0.50 ~ 1.00
P (％)≤: 0.030
S (％)≤: 0.015
Cr (％): 10.85 ~ 12.65
Ni (％): 0.47 ~ 1.03
Mo (％): 0.85 ~ 1.30
W (％): 0.55 ~ 1.30
V (%): 0.17 ~ 0.33
MECHANICAL PROPERTIES UNDER DIFFERENT HEAT TREATED CONDITIONS
Form: bar, flat bar, forge piece
Condition: +A, annealed
Tensile strength σb/MPa: -
Yield strength σ0.2/MPa: -
Elongation δ(％): -
Reduction of area ф(％): -
Hardness | HRB: ≤ 248
Form: bar, flat bar, forge piece
Condition: +HT, tempering (620℃)
Tensile strength σb/MPa: 930
Yield strength σ0.2/MPa: 760
Elongation δ(％): 14.0
Reduction of area ф(％): 32.0
Hardness | HRB: 277 ~ 331
Form: bar,forge piece
Condition: + H, tempering (675℃)
Tensile strength σb/MPa: 825
Yield strength σ0.2/MPa: 585
Elongation δ(％): 17.0
Reduction of area ф(％): 35.
Hardness | HRB: 241~285
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / AOD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered
PRODUCT FORMS & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W70 - 1000mm X L1000-12000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com,
Hot search：10705BU
Previous page：ISO X6NiCrTiMoVB25-15-2
Last page：10705MBU
Total list
Monthly rank
- 50FSX-414
- 16Aquamet 22
- 1510705BU
- 15AMS 5221
- 13Carpenter 20 Mo 4
- 12X12CrNiMoV12-2
- 11Inconel 610
- 10AMS 5354
- 9Incoloy 840
- 8Aquamet 17