1.4914 datasheet,1.4914 chemical,1.4914 heat treatment
Home > Superalloy > Text

1.4914
2014-09-12 09:17:17   Origin:   Remark:0 Click:

Material specifications 1.4914 datasheet, 1.4914 Chemical, 1.4914 Properties from Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
MATERIAL TECHNICAL DATASHEET - AMS 1.4914 
MATERIAL CATEGORY - High temperature high strength steel and superalloy 
MATERIAL SPECIFICATIONS - DIN 17742, 17460, 17480), DIN EN 103021, 10296, 10095
CHEMICAL COMPOSITION (WEIGHT %)
C (%):     0.11 ~ 0.19
Si (%):     0.15 ~ 0.65
Mn (%):   0.20 ~ 1.25
P (%)≤:   0.030
S (%)≤:   0.025
Cr (%):    10.0 ~ 12.0
Ni (%):    0.50 ~ 1.20
Mo (%):   0.40 ~ 1.00
Nb (%):   0.10 ~ 0.60
V (%):     0.10 ~ 0.70
N (%):     0.03 ~ 0.09
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot forming temperature /℃:    1100~850
Heat treatment temperature /℃ | annealing:    750~780    
Heat treatment temperature /℃ | quenching or solution:   1000 ~ 1150 air 
Heat treatment temperature /℃ | tempering: 700~750
Heat treatment temperature /℃ | ageing:    -
Condition: heat treatment
Mechanical property under room temperature |σb/MPa:  930~1130                  
Mechanical property under room temperature  |σs≥/MPa:    785     
Mechanical property under room temperature |δ5≥(%):    10        
Mechanical property under room temperature |Akv(DVM):  27       
Heat stability temperature/℃:   600
Non-scale temperature in air /℃:   -
MECHANICAL PROPERTY UNDER HIGH TEMPERATURE
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|200:    716
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|300:    686
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|400:    618
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|500:    490
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|600:    294
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|700:    -
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|800:    -
Creep rupture strength /MPa,at following time/h and temperature /℃|1000h|600:   245
Creep rupture strength /MPa,at following time/h and temperature /℃|1000h|700:    78
Creep rupture strength /MPa,at following time/h and temperature /℃|1000h|800:    -
Creep rupture strength /MPa,at following time/h and temperature /℃|1000h|900:    -

Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|600:   147
Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|700:    -
Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|800:    -
Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|900:    -
Creep rupture strength /MPa,at following time/h and temperature /℃|100000h|600:   76
Creep rupture strength /MPa,at following time/h and temperature /℃|100000h|700:    -
Creep rupture strength /MPa,at following time/h and temperature /℃|100000h|800:    -
Creep rupture strength /MPa,at following time/h and temperature /℃|100000h|900:    -
  
PRODUCT DESCRIPTION
The alloy is usually produced by BEF + AOD / VD followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the solution annealing condition.
Final heat treatment - heat treatment / QT / solution treatment
TYPICAL APPLICATIONS 
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
Gas turbine
Turbine blade
Fuel nozzle
Heat treating fixture
Furnace muffle
Nuclear reactor
Turbine engine parts - mechanical gears, gear shaft, main axis, blade
Mechanical parts - bolt and nut, fastener
Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.
PRODUCT PROFILE & FORMS
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 3mm to 1000mm
Plate / Sheet steel / Steel strip: 0.1mm to 1500mm
Width: 8mm to 1500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.