Hastelloy C-276 / N10276
2017-02-28 16:50:45 Origin： Remark：0 Click：
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Low-carbon -Ni-Mo-Cr Alloy
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.020
Mn (％): ≤ 1.00
P (％) ≤: 0.025
S (％) ≤: 0.010
Cr (％): 14.5 ~ 16.5
Ni (％): Remainder
Mo (％): 15.0 ~ 17.0
Cu (%): -
W (%): 3.00 ~ 4.50
Fe (%): 4.00 ~ 7.00
Condition: Solution annealed
Tensile strength, σb/≥ MPa: 690
Yield strength, σ0.2/≥ MPa: 283
Elonghation, δ ≥(％): 40.0
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND SHAPES
Round bar (Diameter): 0.20mm to 650mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.