Custom Flo 316HQ
2017-08-26 09:04:10 Origin： Remark：0 Click：
Technical specifications of American high temperature alloys datasheet, Chemical compositions, mechanical properties from Steelmaking, ESR melted, Blooming, Forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
MATERIAL TECHNICAL DATA SHEET - Grade Custom Flo 316HQ
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.030
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％)≤: 0.030
C (％): ≤ 0.030
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％)≤: 0.030
S (％)≤: 0.015
Cr (％): 16.0 ~ 18.5
Cr (％): 16.0 ~ 18.5
Ni (％): 10.0 ~ 14.0
Mo (％): 2.00 ~ 3.00
Co (%): -
Co (%): -
W (%): -
Al (%): -
Al (%): -
Cu (%): 3.00 ~ 4.00
Ti (%): -
Ti (%): -
MECHANICAL PROPERTIES
Tensile strength, σb/≥ MPa: 655
Yield strength, σ0.2/≥ MPa: 525
Elongation, δ ≥(％): 25.0
Reduction of area, ф ≥ (％): 50.0
Hardness | HBW: 217
Elongation, δ ≥(％): 25.0
Reduction of area, ф ≥ (％): 50.0
Hardness | HBW: 217
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged
FORMS AND SHAPES
Round bar (Diameter): 0.50mm to 650mm
Square bar / Flat bar: 3mm to 450mm
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged
FORMS AND SHAPES
Round bar (Diameter): 0.50mm to 650mm
Square bar / Flat bar: 3mm to 450mm
Wire rod (Diameter): 0.20 to 13mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our qualified production engineers. - Email: lh.steel@hotmail.com
You also can reach our sales dept via E-mail: sales@ccsteels.com
Previous page：523H15
Last page：Z2CND25-22Az
Total list
Monthly rank
- 50FSX-414
- 16Aquamet 22
- 1510705BU
- 15AMS 5221
- 13Carpenter 20 Mo 4
- 12X12CrNiMoV12-2
- 11Inconel 610
- 10AMS 5354
- 9Incoloy 840
- 8Aquamet 17