Technical specifications of American high temperature alloys Esshete 1250 datasheet,Esshete 1250 Chemical compositions, Esshete 1250 mechanical properties from Steelmaking, Esshete 1250 ESR melted,Blooming,Grade Esshete 1250 Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - Grade Esshete 1250
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Cr - Ni- W - Fe-base Series alloy
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.06 ~ 0.15
Si (％): 0.20 ~ 1.20
Mn (％): 5.50 ~ 7.00
P (％)≤: 0.030
C (％): 0.06 ~ 0.15
Si (％): 0.20 ~ 1.20
Mn (％): 5.50 ~ 7.00
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 14.0 ~ 16.0
Cr (％): 14.0 ~ 16.0
Ni (％): 9.00 ~ 11.0
Mo (％): 0.80 ~ 1.20
Co (%): -
Co (%): -
W (%): -
Al (%): -
Al (%): -
Cu (%): -
Ti (%): -
Ti (%): -
V (%): 0.15 ~ 0.40
Nb + Ta (%): 0.75 ~ 1.25
B (%): 0.003 ~ 0.009
MECHANICAL PROPERTIES
Tensile strength, σb/≥ MPa: 883
Yield strength, σ0.2/≥ MPa: 745
Elongation, δ ≥(％): 50.0
Reduction of area, ф ≥ (％): -
Hardness | HBW: 223 max.
Reduction of area, ф ≥ (％): -
Hardness | HBW: 223 max.
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged
FORMS AND SHAPES
Round bar (Diameter): 0.50mm to 550mm
Square bar / Flat bar: 3mm to 450mm
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged
FORMS AND SHAPES
Round bar (Diameter): 0.50mm to 550mm
Square bar / Flat bar: 3mm to 450mm
Wire rod (Diameter): 0.20 to 16mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our qualified production engineers.
- Email: lh.steel@hotmail.com
Previous page：T11352
Last page：Z7CND17-11-02
Total list
Monthly rank
- 50FSX-414
- 16Aquamet 22
- 1510705BU
- 15AMS 5221
- 13Carpenter 20 Mo 4
- 12X12CrNiMoV12-2
- 11Inconel 610
- 10AMS 5354
- 9Incoloy 840
- 8Aquamet 17