Specifications Nicrofer 3718 Datasheet, Suppliers Nicrofer 3718 Chemical, Stocklist Nicrofer 3718 mechanical property from Steelmaking,ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - Grade Nicrofer 3718
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Ni-Cr-Fe Superalloy
CHEMICAL COMPOSITION ( Mass Weight % )
C (％): ≤ 0.15
C (％): ≤ 0.15
Si (％): 1.00 ~ 2.00
Mn (％): ≤ 2.00
Mn (％): ≤ 2.00
P (％)≤: 0.035
S (％)≤: 0.020
Cr (％): 15.0 ~ 17.0
Cr (％): 15.0 ~ 17.0
Ni (％): 34.0 ~ 37.0
Mo (％): -
Co (%): -
Co (%): -
W (%): -
Al (%): -
Al (%): -
Cu (%): -
Ti (%): ≤ 0.20
Fe (% ): Balance
TYPICAL MECHANICAL PROPERTIES
Tensile strength, σb/≥ MPa: 648.0
Yield strength, σ0.2/MPa: 285.0
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥ (％): -
Hardness via heat treatment /HBW: 210
Reduction of area, ф ≥ (％): -
Hardness via heat treatment /HBW: 210
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged or Double aged.
FORMS AND DIMENSIONS
Round bar (Diameter): 5.5 ~ 550 mm
Square bar / Flat bar: 3 ~ 350 mm
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged or Double aged.
FORMS AND DIMENSIONS
Round bar (Diameter): 5.5 ~ 550 mm
Square bar / Flat bar: 3 ~ 350 mm
Wire rod (Diameter): 0.10 ~ 16 mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Other sizes can be supplied to meet specific requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our qualified production engineers.E-mail: sales@ccsteels.com.
If you meet further on any technical enquiry or help, pleased to EMAIL our qualified production engineers.E-mail: sales@ccsteels.com.
Total list
Monthly rank
- 50FSX-414
- 16Aquamet 22
- 1510705BU
- 15AMS 5221
- 13Carpenter 20 Mo 4
- 12X12CrNiMoV12-2
- 11Inconel 610
- 10AMS 5354
- 9Incoloy 840
- 8Aquamet 17