Specifications N07080 datasheet, N07080 Chemical, N07080 properties from steelmaking, hot forging, hot rolling, heat treatment, cold working. We also possess advanced precision machining equipments for further processing.
MATERIAL SPECIFICATIONS DATA SHEET - Grade N07080
MATERIAL CATEGORY: Nickel-chromium based superalloy
MATERIAL SPECIFICATIONS - Alloy 80A, W-Nr. 2.4631, W-Nr. 2.4952, UNS N07080, BS 3076
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.10
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.020
S (％)≤: 0.015
Cr (％): 18.0 ~ 21.0
Ni (％): Balance
Ti (％): 1.80 ~ 2.70
Al (％): 1.00 ~ 1.80
Others (%): Co ≤2.00, Cu ≤0.20, Fe ≤3.00, B ≤0.008, Zr ≤0.15
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: heat treatment
Tensile strength, σb/MPa: 1250 Min.
Yield strength, σ0.2≥/MPa: 780
Elongation, δ5 ≥(％): -
Reduction of area, ψ≥(％): 30
Hardness≥: -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatmentalloy similar to alloy 75 but made precipitation hardenable by additions of aluminium and titanium.
The alloy has good corrosion and oxidation resistance and high tensile and creep-rupture properties at temperatures to 1500ºF (815ºC).
Used for gas-turbine components (blades, rings, discs), bolts, tube supports in nuclear generators, exhaust valves in internal combustion engines.
AVAILABILITY
Round bar / flat bar / steel strip / square bar / valve body / ring / plate
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
TYPICAL APPLICATIONS
Gas turbine engineering
Automobile exhaust valves
Die-casting inserts and cores
Nuclear boiler tube parts.
Driveshafts
Gears
Fasteners
Landing and takeoff gear
Missile and ejector systems
Torsion springs
PRODUCT FORMS & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 450mm X W50 - 1000mm X L1000 - 12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com
MATERIAL CATEGORY: Nickel-chromium based superalloy
MATERIAL SPECIFICATIONS - Alloy 80A, W-Nr. 2.4631, W-Nr. 2.4952, UNS N07080, BS 3076
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.10
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.020
S (％)≤: 0.015
Cr (％): 18.0 ~ 21.0
Ni (％): Balance
Ti (％): 1.80 ~ 2.70
Al (％): 1.00 ~ 1.80
Others (%): Co ≤2.00, Cu ≤0.20, Fe ≤3.00, B ≤0.008, Zr ≤0.15
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: heat treatment
Tensile strength, σb/MPa: 1250 Min.
Yield strength, σ0.2≥/MPa: 780
Elongation, δ5 ≥(％): -
Reduction of area, ψ≥(％): 30
Hardness≥: -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatmentalloy similar to alloy 75 but made precipitation hardenable by additions of aluminium and titanium.
The alloy has good corrosion and oxidation resistance and high tensile and creep-rupture properties at temperatures to 1500ºF (815ºC).
Used for gas-turbine components (blades, rings, discs), bolts, tube supports in nuclear generators, exhaust valves in internal combustion engines.
AVAILABILITY
Round bar / flat bar / steel strip / square bar / valve body / ring / plate
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
TYPICAL APPLICATIONS
Gas turbine engineering
Automobile exhaust valves
Die-casting inserts and cores
Nuclear boiler tube parts.
Driveshafts
Gears
Fasteners
Landing and takeoff gear
Missile and ejector systems
Torsion springs
PRODUCT FORMS & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 450mm X W50 - 1000mm X L1000 - 12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com
Hot search：N07080
Previous page：2.4631
Last page：Nimonic 90
Total list
Monthly rank
- 50FSX-414
- 16Aquamet 22
- 1510705BU
- 15AMS 5221
- 13Carpenter 20 Mo 4
- 12X12CrNiMoV12-2
- 11Inconel 610
- 10AMS 5354
- 9Incoloy 840
- 8Aquamet 17