AISI M1 / T13101 Stockist, AISI M1 / T13101 Equivalent Steel
Home > Tool steel > Text

AISI M1 / T13101
2017-09-09 08:44:55   Origin:   Remark:0 Click:

Material Technical Standards ASTM A600 - 2004 high speed tool steel AISI M1 & T13101 datasheet, AISI M1 & T13101 Chemical composition,UNS T13101 Mechanical properties from Steelmaking,ESR melted, Hot blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw test, Cold working, Peeled or rough turned machining. Technical specification - ASTM A600 - 2004. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET:  AISI M1 & T13101

MATERIAL CATEGORY: Mo - W series High speed tool steel
MATERIAL SPECIFICATIONS: ASTM A600 - 2004
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (%):     0.78 ~ 0.88
Si (%):     0.20 ~ 0.50
Mn (%):   0.15 ~ 0.40
P (%)≤:   0.030
S (%)≤:   0.030
Cr (%):    3.50 ~ 4.00
Mo (%):   8.20 ~ 9.20
W (%):    1.40 ~ 2.10
V (%):     1.00 ~ 1.35
HEAT TREATMENT PRACTICE AND HARDNESS
Annealing temperature /℃: 820 ~ 870
Annealed hardness, ≤ HB: 207 ~ 235
Quenching temperature /℃: 1180 ~ 1220
Cooling medium: oil, air
Tempering temperature /℃: 540 ~ 600
Hardness under tempered condition ≥HRC: 65 ~ 60
MELTING PROCESS
This
alloy is generally smelt in Non-vacuum furnace + ESR, Electric Arc Furnace  (EAF), EAF+LF+VD, LF + ESR.
For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.

PRODUCT PROFILE AND AVAILABLE FORMS
Round bar (Diameter): 0.50 to 450mm
Square bar / Flat bar: T3 to 500mm X W3 ~ 1200mm
Wire rod (Diameter):  0.30 to 13mm
Steel strip: THK0.15 ~ 2.50 X W8.0 ~ 185mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.

TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
- Email us:
lh.steel@hotmail.com

Hot search:AISI M1 / T13101

Previous page:T15
Last page:Grade DUMET

Share to: