Description T61207 datasheet, T61207 Chemical, T61207 Properties from Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Official Test Certification: issued by TUV - SGS - BV
MATERIAL TECHNICAL DATASHEET - T61207
MATERIAL CATEGORY - Special use alloy tool steel
MATERIAL SPECIFICATIONS - ASTM A681 -2004
CHEMICAL COMPOSITION (WEIGHT - %)
C (％): 0.95 ~ 1.05
Si (％): 0.20 ~ 0.40
Mn (％): 0.25 ~ 0.45
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 1.25 ~ 1.75
Si (％): 0.20 ~ 0.40
Mn (％): 0.25 ~ 0.45
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 1.25 ~ 1.75
Mo (％): 0.30 ~ 0.50
W (％): -
W (％): -
V (%): -
HEAT TREATMENT PRACTICE AND HARDNESS
Hot working tenperature ℃ /Starting: 980~1090
Hot working tenperature ℃ /Starting: 980~1090
Hot working tenperature ℃ /Ending: 840
Annealing temperature ℃: 790~820
Hardness after annealing ≤HBW: 183~212
Quenching temperature ℃: 820~870
Cooling medium: oil cooled
Tempering temperature ℃: 150~320
Hardness value after tempered /HRC: 64 ~ 56
MELTING PROCESS
This alloy is generally smelt in electric arc furnace (EAF ) or IFF + VD, LF + Electroslag remelting (ESR).
Annealing temperature ℃: 790~820
Hardness after annealing ≤HBW: 183~212
Quenching temperature ℃: 820~870
Cooling medium: oil cooled
Tempering temperature ℃: 150~320
Hardness value after tempered /HRC: 64 ~ 56
MELTING PROCESS
This alloy is generally smelt in electric arc furnace (EAF ) or IFF + VD, LF + Electroslag remelting (ESR).
For a purpose of higher quality, it should be smelt via technology of vacuum refining.
TYPICAL APPLICATIONS
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
HEAT TREATTMENT PRACTICE
The preheating of measuring and cutting tool steel is spheroidizing annealing, final heat treatment is quenching + low temperature tempering and hardness after heat treatment can reach 60~65HRC. When heat treat tool steel grades consideration should be given to hardening temperature, including ratio of heating, cooling and soaking times which will differ due to factors such as the shape and size of each chemical component. Other considerations during heat treatment include the type of furnace, quenching medium and work piece transfer facilities.
The preheating of measuring and cutting tool steel is spheroidizing annealing, final heat treatment is quenching + low temperature tempering and hardness after heat treatment can reach 60~65HRC. When heat treat tool steel grades consideration should be given to hardening temperature, including ratio of heating, cooling and soaking times which will differ due to factors such as the shape and size of each chemical component. Other considerations during heat treatment include the type of furnace, quenching medium and work piece transfer facilities.
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 450mm X W60 - 1000mm X L1000 - 12000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 450mm X W60 - 1000mm X L1000 - 12000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：T61207
Total list
Monthly rank
- 30EN 28
- 1940CMD8
- 17115CrV3
- 15AISI M47 / ASTM M47
- 111.2333
- 11SS14 2140
- 955NCDV7
- 9SK85M / SK5M
- 8Carpenter 158
- 8SKS93