XT80W13Co10Cr4V2
2024-01-29 08:33:57   Origin:   Remark:0 Click:

IS 1570 - 6 Material Specification of High Speed Steel XT80W13Co10Cr4V2 Round bar, Flat bar, Plate, Forgings XT80W13Co10Cr4V2 Stock available, Heat treatment
SPECIFICATION DATASHEET - Grade XT80W13Co10Cr4V2
Material Category - 10.0Co-4Cr-18W-1.5V High Speed
Steel
Material Specifications - IS 1570 - 6 (1996 / 2001 )
Special Melting Process - EAF + VD + LF / BEF + ESR
H S Code For Customs: 7228 4000 / 7228 5000 / 7228 6000
Available Stock on hand - Round bar diameter 60mm
Official Test Certificate - issued by TUV - SGS -  BV

MAIN CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): 0.75 ~ 0.85
Silicon, Si (%): ≤ 0.50
Manganese, Mn (%): ≤ 0.40
Phosphorus, P (%) ≤: 0.030
Sulfur, S (%) ≤: 0.025
Chromium, Cr (%): 3.50 ~ 4.50
Molybdenum, Mo (%): -
Tungsten, W (%): 17.2 ~ 18.7
Vanadiuml, V (%): 1.30 ~ 1.80
Cobalt, Co (%): 9.50 ~ 10.50.

MECHANICAL PROPERTIES - HEAT TREATMENT CYCLE
Hot working tenperature /℃:  1150 ~ 900
Annealing temperature /℃:  820 ~ 850
Quenching temperature /℃:  1300
Cooling medium:  oil or air
Common tempering temperature /℃:  550 ~ 580
Hardness via tempering Temp. HRC: 64 Min.
Hardness via annealing heat treatment /HBW:  230 ~ 300.
 
TECHNICAL SALES ASSISTANCE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special 
material is welcome.

We closely cooperate with the professional inspection partners to strictly control the quality and improve the quality manage system, and guarantee the goods delivery each time. It is proved that we are worth of trusting and will be the strategic partner of the supplying chains in the special steels field.

If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.

Hot search:XT80W13Co10Cr4V2

Previous page:XT122W6Mo5Cr4V3
Last page:最后一页

Share to: