Martensitic Steel Round bar AMS 5763 Forgings, and Rings C-450 Corrosion and Heat resistant 14Cr - 6Ni - 0.8Mo Aged Steel, Solution Treated
TECHNICAL DATASHEET - AMS 5763 & S45000 & C-450
Material Category - Aerospace Material Steel Series
Stock available: Diam. 20 ~ 210mm
Techncial Specifications - AMS 5763D
Material Category - Aerospace Material Steel Series
Stock available: Diam. 20 ~ 210mm
Techncial Specifications - AMS 5763D
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.05
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％)≤: 0.025
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 14.0 ~ 16.0
Molybdenum, Mo (％): 0.50 ~ 1.00
Nickel, Ni (%): 6.00 ~ 7.00
Copper, Cu (％): 1.25 ~ 1.75
Niobium, Nb (%): 8 X C ~ 0.75
Ferrum, Fe (%): remainder
Carbon, C (％): ≤ 0.05
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％)≤: 0.025
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 14.0 ~ 16.0
Molybdenum, Mo (％): 0.50 ~ 1.00
Nickel, Ni (%): 6.00 ~ 7.00
Copper, Cu (％): 1.25 ~ 1.75
Niobium, Nb (%): 8 X C ~ 0.75
Ferrum, Fe (%): remainder
MECHANICAL PROPERTIES AT ROOM TEMP.
Condition: solution treated at 1040 ℃ + 480℃ aged.
Tensile strength, Rm / MPa: 1240 MPa
Yield strength, Rp 0.2 / MPa: 1170 MPa
Elongation, A (％): 10.0
Reduction of area, Z (％): 40.0
Hardness under heat treatment condition | HBW 311 Max.
Yield strength, Rp 0.2 / MPa: 1170 MPa
Elongation, A (％): 10.0
Reduction of area, Z (％): 40.0
Hardness under heat treatment condition | HBW 311 Max.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Basic Electric Furnace (EAF, AOD) or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement. This wire has been used typically for screening and stitching applications requiring good corrosion resistance and which may be subjected to elevated temperatures during fabrication or in service
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on. These products have been used typically for parts requiring both corrosion and oxidation resistance.
This alloy is generally smelt in Basic Electric Furnace (EAF, AOD) or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement. This wire has been used typically for screening and stitching applications requiring good corrosion resistance and which may be subjected to elevated temperatures during fabrication or in service
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on. These products have been used typically for parts requiring both corrosion and oxidation resistance.
PRODUCT PROFILES & DIMENSIONS
Round bar & Disc (diameter): 5.5 to 700mm
Wire rod (diameter): 1.0 ~ 12.5mm
Square bar / Flat bar (Thickness X Width): 10 to 600mm
Length: fixed length, random length, or based on the customer's special requirement.
Round bar & Disc (diameter): 5.5 to 700mm
Wire rod (diameter): 1.0 ~ 12.5mm
Square bar / Flat bar (Thickness X Width): 10 to 600mm
Length: fixed length, random length, or based on the customer's special requirement.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Hot search：AMS 5763 S45000 C-450 Stock Available
Total list
Monthly rank
- 17AMS 5639 & S30400 Corrosion-Resisting Steel
- 15Turbine Blade AE961W Aerospace Martensitic Steel
- 11Free machining Steel AMS 5642 & S34720
- 10SAE 30302 / AMS 5636 Corrosion-Resistant Steel
- 9AMS 5632 & SAE 51440F High-carbon Martensitic Steel
- 9AMS 5649 - J92200 - AISI 316FM Free-machining Steels
- 8FV520B CREEP RESISTANT STEEL
- 8AMS 5678 - S17700 Aged hardening Steel Bar
- 8AMS 5631 - S44002 Martensitic Stainless Steel
- 81.2731 Round bar & ESR Ingot Stock Available