Specifications AMS 5864 datasheet, AMS 5864 Chemical, AMS 5864 properties from steelmaking, hot forging & rolling, heat treatment, cold working. We also possess advanced precision machining equipments for further processing.
AEROSPACE MATERIAL DATASHEET - AMS 5864
MATERIAL CATEGORY: Precipitation hardening type 13Cr-8Ni-2Mo-Al
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.05
Si (％): ≤ 0.10
Mn (％): ≤ 0.20
P (％)≤: 0.010
S (％)≤: 0.008
Cr (％): 12.3 ~ 13.2
Ni (％): 7.50 ~ 8.50
Mo (％): 2.00 ~ 2.50
Al (％): 0.90 ~ 1.35
Si (％): ≤ 0.10
Mn (％): ≤ 0.20
P (％)≤: 0.010
S (％)≤: 0.008
Cr (％): 12.3 ~ 13.2
Ni (％): 7.50 ~ 8.50
Mo (％): 2.00 ~ 2.50
Al (％): 0.90 ~ 1.35
Others (%): N ≤0.01
TYPICAL MECHANICAL PROPERTIES
Form: Bar, forge piece
Condition: H950
Tensile strength, σb/MPa: 1510
Yield strength, σ0.2/MPa: 1420
Elongation, δ(％): 10.0
Reduction of area, ψ(％): 45；35
Hardness, HRC: ≥45
Condition: H950
Tensile strength, σb/MPa: 1510
Yield strength, σ0.2/MPa: 1420
Elongation, δ(％): 10.0
Reduction of area, ψ(％): 45；35
Hardness, HRC: ≥45
Form: Bar, forge piece
Condition: H1000
Condition: H1000
TS, σb/MPa: 1410
YS, σ0.2/MPa: 1310
EL, δ (％): 10.0
RA, ψ(％): 50；40
HRC: ≥43
YS, σ0.2/MPa: 1310
EL, δ (％): 10.0
RA, ψ(％): 50；40
HRC: ≥43
Form: Bar, forge piece
Condition: H1025
Condition: H1025
TS, σb/MPa: 1275
YS, σ0.2/MPa: 1210
EL, δ (％): 11.0
YS, σ0.2/MPa: 1210
EL, δ (％): 11.0
RA, ψ (％): 50.0
HRC: ≥41
HRC: ≥41
Form: Bar, forge piece
Condition: H1050
Condition: H1050
TS, σb/MPa: 1210
YS, σ0.2/MPa: 1140
EL, δ (％): 12.0
RA, ψ (％): 50.0
HRC: ≥40
YS, σ0.2/MPa: 1140
EL, δ (％): 12.0
RA, ψ (％): 50.0
HRC: ≥40
Form: Bar, forge piece
Condition: H1100
Condition: H1100
TS, σb/MPa: 1030
YS, σ0.2/MPa: 930
EL, δ (％): 14.0
RA, ψ (％): 50.0
HRC: ≥34
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
YS, σ0.2/MPa: 930
EL, δ (％): 14.0
RA, ψ (％): 50.0
HRC: ≥34
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 1000mm
Plate / Sheet steel / Steel strip: 0.1mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 1000mm
Plate / Sheet steel / Steel strip: 0.1mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
Previous page：S15700
Last page：A564 Grade XM-13