IS 7806 Gr.1A
2024-02-24 16:21:20 Origin: Remark:0 Click:
IS 7806 Material Specification High temperature & Corrosion Resistant Steel IS 7806 Gr.1A Round bar, flat bar, plate and forgings IS 7806 Gr.1A Stock Available
MATERIAL TECHNICAL DATASHEET - IS 7806 Grade 1A
Official Test Report: issued by TUV - SGS - BV
Special Melting Practice - BEF + AOD / + ESR
HS Code - 72223000 / 72224000
Stock Available - Round bar Diam. 30 ~ 150mm
Material Specifications - IS 7806 (1993 / 1998)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): ≤ 0.15
Silicon, Si (%): ≤ 0.65
Manganese, Mn (%): ≤ 1.00
Phosphorus, P (%) ≤: 0.035
Sulfur, S (%) ≤: 0.025
Chromium, Cr (%): 11.50 ~ 14.00
Nickel, Ni (%): ≤ 1.00
Molybdenum, Mo (%): 0.75 ~ 1.00
Ferrum, Fe (%): Balance
Official Test Report: issued by TUV - SGS - BV
Special Melting Practice - BEF + AOD / + ESR
HS Code - 72223000 / 72224000
Stock Available - Round bar Diam. 30 ~ 150mm
Material Specifications - IS 7806 (1993 / 1998)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): ≤ 0.15
Silicon, Si (%): ≤ 0.65
Manganese, Mn (%): ≤ 1.00
Phosphorus, P (%) ≤: 0.035
Sulfur, S (%) ≤: 0.025
Chromium, Cr (%): 11.50 ~ 14.00
Nickel, Ni (%): ≤ 1.00
Molybdenum, Mo (%): 0.75 ~ 1.00
Ferrum, Fe (%): Balance
MECHANICAL PROPERTY AT ROOM TEMPERATURE
Forms: Round bar, flat bar, forgings and plate
Tensile strength, σb/≥ MPa: 755
Yield strength, σ0.2/MPa: 550
Elongation, δ ≥(%): 15.0
Reduction of area, ф ≥ (%): -
Hardness via annealing /HBW: 239 max.
Forms: Round bar, flat bar, forgings and plate
Tensile strength, σb/≥ MPa: 755
Yield strength, σ0.2/MPa: 550
Elongation, δ ≥(%): 15.0
Reduction of area, ф ≥ (%): -
Hardness via annealing /HBW: 239 max.
PRODUCT DESCRIPTION
The alloy is usually produced by EAF / AOD / BEF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered + Stress relief annealing.
The alloy is usually produced by EAF / AOD / BEF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered + Stress relief annealing.
PROFILE & DIMENSIONS & SERVICE
Round bar & Disc (diameter): 5.5mm to 850mm
Square bar / Flat bar: 10mm to 650mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy / middle plate via hot rolled: T10 ~ 400mm X W70 ~ 1000mm X Lmm
Sheet steel via cold rolled: T0.5 - 6mm X W60 ~ 1000mm X Lmm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 1000mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Round bar & Disc (diameter): 5.5mm to 850mm
Square bar / Flat bar: 10mm to 650mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy / middle plate via hot rolled: T10 ~ 400mm X W70 ~ 1000mm X Lmm
Sheet steel via cold rolled: T0.5 - 6mm X W60 ~ 1000mm X Lmm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 1000mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search:
Previous page:1.6985
Last page:XT152W12Co5V5Cr4Mo1