Specification AIR 9160/C - 1973.Martensitic steel Z15CN17-03 Round bar, flat bar, forgings, ESR melted, Z15CN17-03 on hand, Heat treatment, rough turned,
TECHNICAL SPECIFICATION - AIR 9160C Grade Z15CN17-03
Technical specifications - DGA - AIR 9160/C - 1973
Official test certificate - issued by TUV - SGS
Material type - martensitic sStainless steel
Inventory stock - round bar diam. 15 ~ 180mm
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): 0.12 ~ 0.20
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.025
Chromium, Cr (%): 15.0 ~ 18.0
Molybdenum, Mo (%): -
Nickel, Ni (%): 2.00 ~ 3.00
MECHANICAL PROPERTIES AT ROOM TEMPERATURE
Tensile strength,σb/≥ MPa: 880 ~ 1080
Yield strength, σ0.2/≥ MPa: 690
Elongation, δ ≥(％): 12.0
Reduction of area, ф ≥ (％): -
Impact, AK (J/cm2): -
Annealed hardness | HB: 262 ~ 326
Quenching, 1010,+/-10 Deg, tempering 605, +/-5 Deg.
AVAILABLE FORMS AND DIMENSIONS
Round bar & Disc (Diameter): 5.5 mm to 1000mm
Square bar / Flat bar: 10mm to 500mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Technical specifications - DGA - AIR 9160/C - 1973
Official test certificate - issued by TUV - SGS
Material type - martensitic sStainless steel
Inventory stock - round bar diam. 15 ~ 180mm
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): 0.12 ~ 0.20
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.025
Chromium, Cr (%): 15.0 ~ 18.0
Molybdenum, Mo (%): -
Nickel, Ni (%): 2.00 ~ 3.00
MECHANICAL PROPERTIES AT ROOM TEMPERATURE
Tensile strength,σb/≥ MPa: 880 ~ 1080
Yield strength, σ0.2/≥ MPa: 690
Elongation, δ ≥(％): 12.0
Reduction of area, ф ≥ (％): -
Impact, AK (J/cm2): -
Annealed hardness | HB: 262 ~ 326
Quenching, 1010,+/-10 Deg, tempering 605, +/-5 Deg.
AVAILABLE FORMS AND DIMENSIONS
Round bar & Disc (Diameter): 5.5 mm to 1000mm
Square bar / Flat bar: 10mm to 500mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Hot search：Z15CN17-03