Heat resisting steel for turbine blade 2Cr11Mo1VNbN round bar, forgings stock 2Cr11Mo1VNbN ESR melted, hot forged / rolled, cold drawn, heat treated
TECHNICAL DATA SHEET - 2Cr11Mo1VNbN
STOCK AVAILABLE: round bar diam. 30 ~ 155mm, ESR ingot
MATERIAL CATEGORY: Heat resisting Steel for Turbine blade
Technical standards: GB/T 20878-2007 & GB/T 8732 - 2014
CHEMICAL COMPOSITIONS (mass fraction %)
Carbon, C (％): 0.15 ~ 0.20
Silicon, Si (％): 0.20 ~ 0.60
CHEMICAL COMPOSITIONS (mass fraction %)
Carbon, C (％): 0.15 ~ 0.20
Silicon, Si (％): 0.20 ~ 0.60
Manganese, Mn (％): 0.50 ~ 0.80
Phosphorus, P (％) ≤: 0.020
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 10.50 ~ 11.50
Phosphorus, P (％) ≤: 0.020
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 10.50 ~ 11.50
Molybdenum, Mo (％): 0.80 ~ 1.10
Nickel, Ni (%): 0.30 ~ 0.60
Nitrogen, N (%): 0.04 ~ 0.08
Vanadium, V (%): 0.15 ~ 0.25
Niobium, Nb (%): 0.35 ~ 0.55
Tungsten, W (%): -
Copper, Cu (%): ≤ 0.20
Aluminium, Al (%): ≤ 0.05
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, Rm ≥ MPa: 965
Yield strength, Rp0.2 ≥ MPa: 780
Elongation, A5 ≥(％): 15.0
Yield strength, Rp0.2 ≥ MPa: 780
Elongation, A5 ≥(％): 15.0
Reduction of area, Z (%): 45.0
Impact strength, AKv / J ≥: -
Quenched and tempered - hardness, HB ≤: 285 ~ 321
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered + SRA.
The alloy is usually produced by AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered + SRA.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, you can do EMAIL our qualified production engineers via E-mail: sales@ccsteels.com.
Raw material stock available
Custom 450 / GD450 / XM-25 (S45000), 403 ESR, AISI 616 / 422 ESR, B50A365 / 403Cb+
17-4PH / 630, M-152 / 1.4938 / S151D, FV520B / S143 / 1.4594. X22CrMoV12-1
13Х11Н2B2MФ / AE961W, 11Х11Н2B2MФ / 16Х11Н2B2MФ
AISI 615 / S41800, 15-5PH / XM-12 (S15500), A-286 AISI 660 / S66286
10705BU, 10705MBU, 10705AJ, S132, S131, S111, S159, S154
Hot search：2Cr11Mo1VNbN