AIR9160C 30NCD16
2016-12-13 09:36:22 Origin： Remark：0 Click：
High tensile strength steel 30NCD16 Round bar, flat bar, forgings AIR9160C 30NCD16 Steelmaking, ESR melted, Hot forging / rolling, Heat treatment, Straightening, 100% Ultrasonic test
TECHNICAL SPECIFICATION - AIR 9160C Grade 30NCD16
TECHNICAL SPECIFICATION: DGA - AIR 9160/C - 1973
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS
MATERIAL CATEGORY: high tensile strength structural steel
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): 0.26 ~ 0.33
Silicon, Si (％): 0.10 ~ 0.40
Manganese, Mn (％): 0.20 ~ 0.60
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.020
Chromium, Cr (%): 1.20 ~ 1.50
Molybdenum, Mo (%): 0.30 ~ 0.60
Nickel, Ni (%): 3.30 ~ 4.30
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Tensile strength,σb/≥ MPa: 1080 ~ 1230
Yield strength, σ0.2/≥ MPa: 880
Elongation, δ ≥(％): 10.0
Reduction of area, ф ≥ (％): 45.0
Impact, AK (J/cm2): -
Annealed hardness | HB: 320 ~ 360
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Tensile strength,σb/≥ MPa: 1080 ~ 1230
Yield strength, σ0.2/≥ MPa: 880
Elongation, δ ≥(％): 10.0
Reduction of area, ф ≥ (％): 45.0
Impact, AK (J/cm2): -
Annealed hardness | HB: 320 ~ 360
Quenching, 850,+/-10 Deg. tempering 585, +/-5 Deg
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 5.5 mm to 500mm
Square bar / Flat bar: 3mm to 500mm
Steel strip: T0.20 ~ 3mm X W10 ~ 1000mm X Coil
Forging piece: stepped shafts, other different shapes based on OEM.
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 5.5 mm to 500mm
Square bar / Flat bar: 3mm to 500mm
Steel strip: T0.20 ~ 3mm X W10 ~ 1000mm X Coil
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.