ASTM A387 type 5
2019-09-02 09:41:10 Origin： Remark：0 Click：
Round bar ASTM A387 Grade 5, Flat bars A387 Grade 5, Plate A387 Grade 5 strip property from Steel making, ESR melted, Blooming, Hot forging, Hot rolling, Heat treated, Straightening, 100% Ultrasonic test, Cold working or rough turned machining. Technical specification - ASTM A387 - 2017.
TECHNICAL DATA SHEET - ASTM A387 Grade 5
MATERIAL TECHNICAL STANDARDS: ASTM A387 - 2017
Mn (％): 0.30 ~ 0.60
Si (％): ≤ 0.50
Si (％): ≤ 0.50
P (％)≤: 0.025
S (％)≤: 0.025
Cr (%): 4.00 ~ 6.00
Mo (%): 0.45 ~ 0.65
S (％)≤: 0.025
Cr (%): 4.00 ~ 6.00
Mo (%): 0.45 ~ 0.65
Ni (%): -
V (%): -
Nb (%): -
Cu (%): -
B (%): -
W (%): -
Al (%): -
Ti (%): -
TYPICAL MECHANICAL PROPERTIES
Tensile strength, σb/≥ MPa: 415 ~ 585
Yield strength, σ0.2/MPa: 205
Elongation, δ ≥(％): 18.0
Reduction of area, ф ≥ (％): 45.0
Hardness via heat treatment /HBW: 255 MAX.
Reduction of area, ф ≥ (％): 45.0
Hardness via heat treatment /HBW: 255 MAX.
PRODUCT DESCRIPTION
The alloy is usually produced by BEF /EAF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm to 610mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W10 - 1500mm X L1000-12000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
The alloy is usually produced by BEF /EAF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm to 610mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W10 - 1500mm X L1000-12000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Previous page：ASTM A387 type 22L
Last page：S50200