ASTM A182 Specifications F22 Class 3 Material offers a good toughness, F22 round bar, plate, flat bar Blooming, Hot forging, Hot rolling, Heat treatment, 100% Ultrasonic test.
TECHNICAL DATA SHEET - ASTM A182 Grade F22 Class 3
MATERIAL TECHNICAL STANDARDS: ASTM A182 - 2018
MATERIAL TYPE: 2.25Cr - 1.0Mo Alloy steel
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): 0.05 ~ 0.15
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): 0.05 ~ 0.15
Manganese, Mn (％): 0.30 ~ 0.60
Silicon, Si (％): ≤ 0.50
Silicon, Si (％): ≤ 0.50
Phosphorus, P (％) ≤: 0.020
Sulfur, S (％) ≤: 0.020
Chromium, Cr (%): 2.00 ~ 2.50
Molybdenum, Mo (%): 0.85 ~ 1.15
Sulfur, S (％) ≤: 0.020
Chromium, Cr (%): 2.00 ~ 2.50
Molybdenum, Mo (%): 0.85 ~ 1.15
Nickel, Ni (%): -
Niobium, Nb (%): -
TYPICAL MECHANICAL PROPERTIES
Tensile strength, σb/≥ MPa: 515
Yield strength, σ0.2/MPa: 310
Elongation, δ ≥(％): 20.0
Reduction of area, ф ≥ (％): 30.0
Hardness via heat treatment /HBW: 156 ~ 207
Reduction of area, ф ≥ (％): 30.0
Hardness via heat treatment /HBW: 156 ~ 207
HEAT TREATMENT PRACTICE
Condition: annealed 900 Deg. C
Cooling medium: furnace cool
Tempering temperature: -
Condition: normalize and tempered 900 Deg. C
Cooling medium: air cool
Tempering temperature: 675 Deg. C
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / BEF + AOD / EAF + VD + LF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.50mm to 650mm
Square bar / Flat bar: 10mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 ~ 400mm X W60 ~ 1000mm X L1000 ~ 3500mm
Forging piece: stepped shafts, other different shapes based on OEM.
Round bar / Wire rod (Diameter): 5.50mm to 650mm
Square bar / Flat bar: 10mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 ~ 400mm X W60 ~ 1000mm X L1000 ~ 3500mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical inquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical inquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Previous page：Grade F22 Class 1
Last page：STS416