Aerospace ESR Quality Steel AMS 6305 Round bar, flat bar, plate ESR refined, AMS 6305 Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working
TECHNICAL DATA SHEET - Grade AMS 6305
MELTING PRACTICE: Consumable electrode remelted
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (mass weight %)
Carbon, C (％): 0.40 ~ 0.50
Manganese, Mn (％): 0.40 ~ 0.70
Silicon, Si (％): 0.15 ~ 0.35
Phosphorus, P (％)≤: 0.015
Sulfur, S (％)≤: 0.015
Chromium, Cr (%): 0.80 ~ 1.10
Vanadium, V (%): 0.25 ~ 0.35
Molybdenum, Mo (%): 0.45 ~ 0.65
Carbon, C (％): 0.40 ~ 0.50
Manganese, Mn (％): 0.40 ~ 0.70
Silicon, Si (％): 0.15 ~ 0.35
Phosphorus, P (％)≤: 0.015
Sulfur, S (％)≤: 0.015
Chromium, Cr (%): 0.80 ~ 1.10
Vanadium, V (%): 0.25 ~ 0.35
Molybdenum, Mo (%): 0.45 ~ 0.65
Nickel, Ni (%): ≤ 0.25
Copper, Cu (%): ≤ 0.35
Pb (%): ≤ 0.001 (10PPM)
MECHANICAL PROPERTY AND HARDNESS
Quenching temperature /℃:
Tempering temperature /℃:200
Tensile strength,σb/≥ MPa: 865 max.
MECHANICAL PROPERTY AND HARDNESS
Quenching temperature /℃:
Tempering temperature /℃:200
Tensile strength,σb/≥ MPa: 865 max.
Yield strength, σ0.2/≥ MPa: -
Elongation, δ ≥(％): -
Reduction of area, ф ≥(％): -
Hardness in condition of annealing +A: HB248 max.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in VIM + Electroslag remelting (ESR / VAR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 450mm
Square bar / Flat bar: 10mm to 650mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Elongation, δ ≥(％): -
Reduction of area, ф ≥(％): -
Hardness in condition of annealing +A: HB248 max.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in VIM + Electroslag remelting (ESR / VAR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 450mm
Square bar / Flat bar: 10mm to 650mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.