Superalloy X7CrNiMoBNb16-16 datasheet, X7CrNiMoBNb16-16 Chemical, DIN X7CrNiMoBNb16-16 properties from Steelmaking, ESR melted, Blooming, hot forging & rolling, Heat treat, Straighten, Ultrasonic test, Cold working or Machined. We also possess the advanced precision machining equipments for further processing, just let us know what you inquire.
MATERIAL SPECIFICATIONS - DIN X7CrNiMoBNb16-16
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
MATERIAL CATEGORY - High temperature high strength steel and superalloy
PRODUCT DESCRIPTION
The alloy is usually produced by AOD/VIM/VOD followed by electroslag refining (ESR) or VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the solution annealing condition.
Final heat treatment - heat treatment / QT / solution treatment
MATERIAL SPECIFICATIONS - DIN 17742, 17460, 17480, DIN EN 103021, 10296, 10095
AVAILABLE SHAPES
Round bar / flat bar / square bar / valve body / ring / plate
Bright - peeled + polishing /centerless grinding /peeled + slidabrading
Forged - ring /pipe casing /discs /shaft
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.04 ~ 0.10
Si (％): 0.30 ~ 0.60
Mn (％): ≤ 1.50
P (％)≤: 0.045
S (％)≤: 0.030
Cr (％): 15.5 ~ 17.5
Ni (％): 15.5 ~ 17.5
Mo (％): 1.60 ~ 2.00
Nb + Ta (％): 10×C％ ~ 1.20
Si (％): 0.30 ~ 0.60
Mn (％): ≤ 1.50
P (％)≤: 0.045
S (％)≤: 0.030
Cr (％): 15.5 ~ 17.5
Ni (％): 15.5 ~ 17.5
Mo (％): 1.60 ~ 2.00
Nb + Ta (％): 10×C％ ~ 1.20
B (%): 0.05～0.10
Hot forming temperature /℃: 1150～850
Heat treatment temperature /℃ | annealing: -
Heat treatment temperature /℃ | quenching or solution: 1100~ 1150 air/water
Heat treatment temperature /℃ | tempering: 750~800
Heat treatment temperature /℃ | ageing: -
Condition: precipitation hardening
Mechanical property under room temperature |σb/MPa: 650~850
Mechanical property under room temperature |σs≥/MPa: 500
Mechanical property under room temperature |σs≥/MPa: 500
Mechanical property under room temperature |δ5≥(％): 16
Mechanical property under room temperature |Akv(DVM): 48
Heat stability temperature/℃: 650
Non-scale temperature in air /℃: 750
MECHANICAL PROPERTY UNDER HIGH TEMPERATURE
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|200: 432
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|300: 393
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|400: 353
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|500: 314
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|600: 255
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|700: -
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|800: -
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|300: 393
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|400: 353
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|500: 314
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|600: 255
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|700: -
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|600: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|700: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|600: 344
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|700: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|600: 344
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|700: -
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|600: 275
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|600: 275
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|700: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|900: -
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
Gas turbine
Turbine blade
Fuel nozzle
Heat treating fixture
Furnace muffle
Nuclear reactor
Turbine blade
Fuel nozzle
Heat treating fixture
Furnace muffle
Nuclear reactor
Turbine engine parts - mechanical gears, gear shaft, main axis, blade
Mechanical parts - bolt and nut, fastener
Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.
These materials must stand up to high heat, extreme oxidation potential and recycling.
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 3mm to 1000mm
Plate / Sheet steel / Steel strip: 0.1mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to email or call our resident team of qualified production engineers. Email: sales@ccsteels.com
Hot search：X7CrNiMoBNb16-16
Previous page：2.4983
Last page：X8CrNiMoBNb16-16
Total list
Monthly rank
- 50FSX-414
- 16Aquamet 22
- 1510705BU
- 15AMS 5221
- 13Carpenter 20 Mo 4
- 12X12CrNiMoV12-2
- 11Inconel 610
- 10AMS 5354
- 9Incoloy 840
- 8Aquamet 17