Alloy 59
2016-07-25 13:44:35 Origin： Remark：0 Click：
Specifications Grade 59 datasheet, Round bar N06059 VIM, ESR melted, Blooming, hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, cold machined.
TECHNICAL DATASHEET - Grade Alloy 59
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: American high temperature alloy and other special alloy
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): ≤ 0.010
Silicon, Si (％): ≤ 0.10
Manganese, Mn (％): ≤ 0.50
Phosphorus, P (％)≤: 0.015
Sulfur, S (％)≤: 0.005
Chromium, Cr (％): 22.0 ~ 24.0
Nickel, Ni (％): Balance
Molybdenum, Mo (％): 15.0 ~ 16.5
Silicon, Si (％): ≤ 0.10
Manganese, Mn (％): ≤ 0.50
Phosphorus, P (％)≤: 0.015
Sulfur, S (％)≤: 0.005
Chromium, Cr (％): 22.0 ~ 24.0
Nickel, Ni (％): Balance
Molybdenum, Mo (％): 15.0 ~ 16.5
Cobalt, Co (%): ≤ 0.30
Tungsten, W (%): -
Aluminum, Al (%): -
Copper, Cu (%): -
Titanium, Ti (%): -
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
Heat treating fixture, Furnace muffle, Nuclear reactor.
Turbine engine parts - mechanical gears, gear shaft, main axis, blade.
Mechanical parts - bolt and nut, fastener, Gas turbine, Turbine blade, Fuel nozzle.
Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.
These materials must stand up to high heat, extreme oxidation potential and recycling.
PRODUCT DESCRIPTION
The alloy is usually produced by VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
The alloy is usually produced by VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
FORMS AND DIMENSIONS
Round bar (Diameter): 5.50mm to 300mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T60 - 350mm X W50 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T60 - 350mm X W50 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com
Previous page：6150H / H61500
Last page：6118H H61180
Total list
Monthly rank
- 50FSX-414
- 16Aquamet 22
- 1510705BU
- 15AMS 5221
- 13Carpenter 20 Mo 4
- 12X12CrNiMoV12-2
- 11Inconel 610
- 10AMS 5354
- 9Incoloy 840
- 8Aquamet 17