N06617
2017-03-14 15:19:41 Origin： Remark：0 Click：
Specifications N06617 Datasheet, Inventory N06617 Chemical, Stocklist N06617 Properties from Steelmaking, ESR melted, Blooming, Forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - ASTM B564-04 Grade UNS N06617
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY - Ni-Cr-Co-Mo Alloy
MELTING PROCESS - EAF + AOD / VIM + ESR
Official Test Certificate - issued by TUV - SGS - BV
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.05 ~ 0.15
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％) ≤: 0.030
S (％) ≤: 0.015
Cr (％): 20.0 ~ 24.0
Ni (％): 44.5 min.
Mo (％): 8.00 ~ 10.0
Cu (%): ≤ 0.50
Mn (％): ≤ 1.00
P (％) ≤: 0.030
S (％) ≤: 0.015
Cr (％): 20.0 ~ 24.0
Ni (％): 44.5 min.
Mo (％): 8.00 ~ 10.0
Cu (%): ≤ 0.50
Al (%): 0.80 ~ 1.50
Ti (%): ≤ 0.60
Ce (%): -
Zr (%): -
Y (%): -
Nb (%): -
Co (%): 10.0 ~ 15.0
V (%): -
N (%): -
B (%): ≤ 0.006
La (%): -
W (%): -
W (%): -
Ta (%): -
Fe (%): 3.0 max.
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: Solution annealed
Tensile strength, σb/≥ MPa: 655
Yield strength, σ0.2/≥ MPa: 241
Elonghation, δ ≥(％): 35.0
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND DIMENSIONS AVAILABLE
Round bar (Diameter): 5.5mm to 400mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T15 - 300mm X W10 - 1000mm X L1000 - 12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W6 - 800mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Fe (%): 3.0 max.
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: Solution annealed
Tensile strength, σb/≥ MPa: 655
Yield strength, σ0.2/≥ MPa: 241
Elonghation, δ ≥(％): 35.0
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND DIMENSIONS AVAILABLE
Round bar (Diameter): 5.5mm to 400mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T15 - 300mm X W10 - 1000mm X L1000 - 12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W6 - 800mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：N06617
Previous page：ASTM A437 Gr.B4C
Last page：Inconel 617