Specifications AM-355 datasheet, AM-355 Chemical, AM-355 Properties from Steelmaking, ESR melted, Blooming, Forging, Hot rolling, Heat treat, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power.100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
MATERIAL TECHNICAL DATA SHEET - AM-355
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
MATERIAL CATEGORY - American high temperature alloy and other special alloys
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.10 ~ 0.15
Si (％): ≤ 0.50
Mn (％): 0.50 ~ 1.25
P (％)≤: 0.025
S (％)≤: 0.010
Cr (％): 15.0 ~ 16.0
Ni (％): 4.00 ~ 5.00
Mo (％): 2.50 ~ 3.20
Co (%): -
Mo (％): 2.50 ~ 3.20
Co (%): -
Nb + Ta (%): 0.15 ~ 0.50
W (%): -
Al (%): -
Cu (%): -
Ti (%): -
N (％): -
W (%): -
Al (%): -
Cu (%): -
Ti (%): -
N (％): -
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: annealing
Tensile strength, σb/MPa: ≤1380
Yield strength, σ0.2/MPa: 585~620
Elongation, δ(％): 8~12
Elongation, δ(％): 8~12
Reduction of area, ф(％): -
Form: plate,sheet,strip
Condition: H850
TS, σb/MPa: 1175
YS, σ0.2/MPa: 1030
E, δ(％): 2~8
A, ф(％): -
E, δ(％): 2~8
A, ф(％): -
Form: plate,sheet,strip
Condition: H1000
TS, σb/MPa: 1140
YS, σ0.2/MPa: 1000
E, δ(％): 2~8
A, ф(％): -
E, δ(％): 2~8
A, ф(％): -
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
FORMS AND DIMENSIONS
Round bar (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 500mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
FORMS AND DIMENSIONS
Round bar (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 500mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail us: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail us: sales@ccsteels.com
Hot search：AM-355
Previous page：Z5NCTDV26-15B
Last page：Aqualloy
Total list
Monthly rank
- 50FSX-414
- 16Aquamet 22
- 1510705BU
- 15AMS 5221
- 13Carpenter 20 Mo 4
- 12X12CrNiMoV12-2
- 11Inconel 610
- 10AMS 5354
- 9Incoloy 840
- 8Aquamet 17