Turbine blade steel 10705MBU peeled round bar, milled flat bar, 10705MBU Stockist forgings, ESR melting, hot bloomed, forged, rolled, heat treated
TECHNICAL DATA SHEET - 10705MBU
Official test report: issued by TUV - SGS - CNAS
Material category: heat resisting steel for turbine blades
Material category: heat resisting steel for turbine blades
Material technical specifications: GTC-0029 / Ref. GB/T 8732 - 2014
Stock available: round bar 50 ~ 160 mm
TYPICAL CHEMICAL COMPOSITIONS (mass fraction - %)
Carbon, C (％): 0.12 ~ 0.16
Silicon, Si (％): ≤ 0.06
Carbon, C (％): 0.12 ~ 0.16
Silicon, Si (％): ≤ 0.06
Manganese, Mn (％): 0.30 ~ 0.70
Phosphorus, P (％): ≤ 0.020
Sulfur, S (％): ≤ 0.015
Chromium, Cr (％): 10.0 ~ 11.0
Phosphorus, P (％): ≤ 0.020
Sulfur, S (％): ≤ 0.015
Chromium, Cr (％): 10.0 ~ 11.0
Molybdenum, Mo (％): 0.35 ~ 0.50
Nickel, Ni (%): 0.35 ~ 0.65
Vanadium, V (%): 0.14 ~ 0.20
Tungsten, W (%): 1.50 ~ 1.90
Copper, Cu (%): ≤ 0.50
Nitrogen, N (%): 0.04 ~ 0.08
Niobium, Nb (%): 0.05 ~ 0.11
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: QT1
Quenching ≥ 1100 Deg., oil cooling
Tempering ≥ 620 Deg., air cooling
Tensile strength, Rm ≥ MPa: 930
Yield strength, Rp0.2 ≥ MPa: 760
Elongation, A5 ≥ (％): 14.0
Yield strength, Rp0.2 ≥ MPa: 760
Elongation, A5 ≥ (％): 14.0
Reduction of area, Z (%): 32.0
Impact strength, AKv2 / J ≥: 20
Heat treated = Q + T hardness, HBW: 277 ~ 331
PRODUCT DESCRIPTION
10705MBU alloy is usually produced by AOD / BEF / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - quenched and tempered + SRA.
10705MBU alloy is usually produced by AOD / BEF / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - quenched and tempered + SRA.
ADVANTAGED STOCK ITEMS
High alloy and superalloy for turbine blade
ASTM A565 Grade 616 / 422 / S42200, Grade 615/S41800, XM-32 / S64152
17-4PH / 630 / 1.4542, 631, 851, 961, WB36, D6-AC, D6A.
1.4980, 1.4922, 1.4923, 1.4935, 1.4938, 1.4913
Forms: Bars, Forge piece, Ring,
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, you can contact our qualified production engineers. via Email: sales@ccsteels.com.
If you meet further on any technical enquiry or help, you can contact our qualified production engineers. via Email: sales@ccsteels.com.
Hot search：10705MBU
Previous page：10705BU
Last page：X21CrMoV12-1
Total list
Monthly rank
- 44ASTM A565 type 616HT
- 40ASTM A890 Grade 1B
- 39T122
- 19N06102
- 19Z15CN24-13
- 16X8CrNiMoVNb16-13
- 15X1CrNiMoCu12-5-2
- 15S41425
- 15STS321
- 141.6359