K94100
2019-08-02 09:21:45   Origin:   Remark:0 Click:

Material specification K94100 datasheet, K94100 Chemical, K94100 Ring forging, Bar, Wire rod, K94100 Sheet - steelmaking, ESR, Blooming, K94100 hot Forging, hot Rolling, Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
TECHNICAL DATASHEET - UNS K94100

OFFICIAL TEST CERTIFICATE: issued by TUV - SGS BV
MATERIAL CATEGORY: Nickel iron alloy
CHEMICAL COMPOSITION (WEIGHT %)
C (%):     ≤ 0.05
Si (%):     ≤ 0.030
Mn (%):   ≤ 0.80
P (%)≤:   0.025
S (%)≤:   0.015
Cr (%):    ≤  0.25
Ni (%):    41.0 min.
Al (%):    ≤ 0.10
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Solution treatment temperature: 1020~1070℃
Tensile strength, σb≥ /MPa: 490
Yeild strength, σ0.2 ≥/MPa: 250
Elongation, δ≥(%): 43.0
Impact, Akv ≥/J: -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
PRODUCT PROFILE
Round bar (Diameter): 0.50mm to 450mm
Square bar / Flat bar: 3mm to 500mm
Wire rod (Diameter):  5.5mm to 16mm
Length: Fixed length or random length or based on the customer's special requirement.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.