1.3917 Stockist, 1.3917 Equivalent Steel

1.3917
2019-08-02 09:16:47   Origin:   Remark:0 Click:

Round bars 1.3917 Stock list, Flat bars 1.3917 Plate, 1.3917 Wire rod Sheet - steelmaking, ESR, Blooming, hot Forging, hot Rolling, Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
TECHNICAL DATASHEET - Grade DIN 1.3917

OFFICIAL TEST CERTIFICATE: issued by TUV - SGS BV
MATERIAL CATEGORY: Nickel iron alloy
CHEMICAL COMPOSITION (Mass weight - %)
C (%):     ≤ 0.12
Si (%):     ≤ 0.30
Mn (%):   ≤ 0.80
P (%)≤:   0.025
S (%)≤:   0.015
Cr (%):    ≤ 0.25
Ni (%):    41.0 ~ 43.0
Al (%):    ≤ 0.10
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Solution treatment temperature: 1020 ~ 1070℃
Tensile strength, σb≥ /MPa: 510
Yeild strength, σ0.2 ≥/MPa: 290
Elongation, δ≥(%): 43.0
Impact, Akv ≥/J: -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment or solution + aged.
PROFILE AND DIMENSIONS
Round bar (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 500mm
Wire rod (Diameter):  5.5mm to 16mm
Length: Fixed length or random length or based on the customer's special requirement.
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 400mm X L, or in coil form.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers.E-mail: sales@ccsteels.com

Hot search:1.3917

Previous page:ASTM F30 / Nilo 42
Last page:K94100

Share to: