S63198
2020-05-11 10:54:41 Origin： Remark：0 Click：
Inventory S63198 Datasheet, Chemical S63198 Suppliers, Properties S63198 Forgings - Technical specifications ASTM A453 From Melting, ESR & VAR technique, Hot Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic flaw detection test.
TECHNICAL DATA SHEET - UNS S63198
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
MATERIAL CATEGORY - Martensitc stainless steel
MATERIAL CATEGORY - Martensitc stainless steel
SPECIFICATIONS -:AMS 5526, ASTM A453
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.28 ~ 0.35
Si (％): 0.30 ~ 0.80
Mn (％): 0.75 ~ 1.50
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 18.0 ～ 21.0
Ni (％): 8.00 ～ 11.0
Mo (％): 1.00 ~ 1.75
W (％): 1.00 ~ 1.75
Ti (%): 0.10 ~ 0.35
Nb (%): 0.25 ~ 0.60
Others (%): Cu ≤0.50
TYPICAL MECHANICAL PROPERTY
Tensile strength, σb/≥ MPa: 835
Yield strength, σ0.2/≥ MPa: 570
Elongation, δ ≥(％): 43.0
Reduction of area, ф ≥ (％): -
Hardness | HRB: -
APPLICATION FIELD
Tall oil distillation columns and equipment
Food processing equipment
Hydrometallurgy, heat exchangers
PRODUCT MELTING PROCESS
The alloy is usually produced by BEF AOD / EAF VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Heat treatment - solution annealing or ageing treatment
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.28 ~ 0.35
Si (％): 0.30 ~ 0.80
Mn (％): 0.75 ~ 1.50
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 18.0 ～ 21.0
Ni (％): 8.00 ～ 11.0
Mo (％): 1.00 ~ 1.75
W (％): 1.00 ~ 1.75
Ti (%): 0.10 ~ 0.35
Nb (%): 0.25 ~ 0.60
Others (%): Cu ≤0.50
TYPICAL MECHANICAL PROPERTY
Tensile strength, σb/≥ MPa: 835
Yield strength, σ0.2/≥ MPa: 570
Elongation, δ ≥(％): 43.0
Reduction of area, ф ≥ (％): -
Hardness | HRB: -
APPLICATION FIELD
Tall oil distillation columns and equipment
Food processing equipment
Hydrometallurgy, heat exchangers
PRODUCT MELTING PROCESS
The alloy is usually produced by BEF AOD / EAF VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Heat treatment - solution annealing or ageing treatment
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：S63198
Total list
Monthly rank
- 50FSX-414
- 16Aquamet 22
- 1510705BU
- 15AMS 5221
- 13Carpenter 20 Mo 4
- 12X12CrNiMoV12-2
- 11Inconel 610
- 10AMS 5354
- 9Incoloy 840
- 8Aquamet 17