AMS 5747
2024-11-18 08:44:55 Origin： Remark：0 Click：
AMS 5747 Hardened by a complex precipitation of intermetallic phases, the alloy combines corrosion resistance with excellent tensile and stress rupture strength.
MATERIAL DESIGNATION - AMS 5747
Material Category - Aerospace Material Steel Series
Stock available: Diam. 40 ~ 120mm
Techncial Specifications - AMS 5747e
HS Code for Customs - 72221100 / 72221900 / 72223000
Official Test Report - issued by TUV - SGS - BV
TYPICAL CHEMICAL ELEMENTS (mass fraction %)
Carbon, C (％): ≤ 0.08
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.020
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 14.0 ~ 17.0
Nickel, Ni (％): 70.0 min.
Molybdenum, Mo (％): -0
Aluminum, Al (&): 0.40 ~ 1.00
Titanium, Ti (%): 2.25 ~ 2.75
Niobium, Nb (%): 0.70 ~ 1.20
Cobalt, Co (％) ≤: 1.00
Ferrum, Fe (%): 5.00 ~ 9.00
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 14.0 ~ 17.0
Nickel, Ni (％): 70.0 min.
Molybdenum, Mo (％): -0
Aluminum, Al (&): 0.40 ~ 1.00
Titanium, Ti (%): 2.25 ~ 2.75
Niobium, Nb (%): 0.70 ~ 1.20
Cobalt, Co (％) ≤: 1.00
Ferrum, Fe (%): 5.00 ~ 9.00
MECHANICAL PROPERTIES AT ROOM TEMP.
Condition: solution treated at 1035 ℃.and then at 580°C for 3h in air
Tensile strength, Rm / MPa: 1130 min.
Yield strength, Rp 0.2 / MPa: 730
Elongation, A (％): 20.0
Reduction of area, Z (％): 25.0
Hardness solution condition | HRC: -
MELTING PROCESS & APPLICATION
AMS 5747 alloy is generally smelt in Basic Electric Furnace (EAF, AOD) or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement. This wire has been used typically for screening and stitching applications requiring good corrosion resistance and which may be subjected to elevated temperatures during fabrication or in service
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on. These products have been used typically for parts requiring both corrosion and oxidation resistance.
AMS 5747 alloy is generally smelt in Basic Electric Furnace (EAF, AOD) or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement. This wire has been used typically for screening and stitching applications requiring good corrosion resistance and which may be subjected to elevated temperatures during fabrication or in service
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on. These products have been used typically for parts requiring both corrosion and oxidation resistance.
ADVANTAGE & SUPERIOR SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
CNC saw cutting. Marking by stamping or printing. Third party inspection service. Export packing / Export documents.
Transport by Track, Sea, Courier (FedEx, UPS, DHL) and Air Cargo.
We closely cooperate with the professional inspection partners to strictly control the quality and improve the quality manage system, and guarantee the goods delivery each time. It is proved that we are worth of trusting and will be the strategic partner of the supplying chains in the special steels field.
PRODUCT PROFILES & DIMENSIONS
Round bar & rod & disc (diameter): 5.5 to 800mm
Wire rod (diameter): 1.0 ~ 12.5mm
Square bar / Flat bar (Thickness X Width): 10 to 600mm
Length: fixed length, random length, or based on the customer's special requirement.
TECHNICAL SALES ASSISTANCE & SERVICE
If you are interested in our products or services, pleased to EMAIL ( sales@ccsteels.com ) our qualified production engineers or sales department.