ASTM L3 /T61203 Stockist, ASTM L3 /T61203 Equivalent Steel
Home > Tool steel > Text

ASTM L3 /T61203
2015-12-30 10:14:02   Origin:   Remark:0 Click:

Technical specification of ASTM standards special use alloy tool steel L3 datasheet,ASTM L3 Chemical compositions, ASTM L3 Mechanical properties from Steelmaking, ESR melted, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or rough turned machining. Technical specification - ASTM A681-2004. We also possess the advanced precision machining equipments for catering for your different special requirements.
 
 
Official Test Certification: issued by TUV - SGS BV

TECHNICAL SPECIFICATION / MATERIAL DATASHEET: ASTM L3 /T61203
MATERIAL CATEGORY:  Special use alloy tool steel
MATERIAL SPECIFICATIONS:  ASTM A681 -2004
CHEMICAL COMPOSITION (WEIGHT - %)
C (%):     0.95~1.10
Si (%):     0.10~0.50
Mn (%):   0.25~0.80

P (%)≤:   0.030
S (%)≤:   0.030
Cr (%):    1.30~1.70
Mo (%):   -
W (%):     -
V (%):      0.10~0.30
HEAT TREATMENT PRACTICE AND HARDNESS
Hot working tenperature ℃ /Starting:   980~1090
Hot working tenperature ℃ /Ending:     840
Annealing temperature ℃:                   790~820
Hardness after annealing ≤HBW:          174~201
Quenching temperature ℃:                  770~820
Cooling medium:                                 water cooled
Tempering temperature ℃:                 150~320
Hardness value after tempered /HRC:    63 ~ 56

MELTING PROCESS 
This alloy is generally smelt in electric arc furnace  (EAF ) or IFF + VD, LF + Electroslag remelting (ESR).
For a purpose of higher quality, it should be smelt via technology of vacuum refining.
TYPICAL APPLICATIONS
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutting tools
Mechanical parts 
Air hammer tools
Piercing tools
HEAT TREATTMENT PRACTICE
The preheating of measuring and cutting
tool steel is spheroidizing annealing, final heat treatment is quenching + low temperature tempering and hardness after heat treatment can reach 60~65HRC. When heat treat tool steel grades consideration should be given to hardening temperature, including ratio of heating, cooling and soaking times which will differ due to factors such as the shape and size of each chemical component. Other considerations during heat treatment include the type of furnace, quenching medium and work piece transfer facilities.
FEATURES AND CLASSIFICATIONS
Hot-work die divides into several main types, such as hammer forging, die forging, extrusion and die casting, including hot forging die, press machine forging die, stamping die, hot-extrusion die, metal die-casting mould. Heat distortion mould not only supports huge mechanical stress, but also thermal stress during working repeatedly. Hot-work die steel should have not only high hardness, red hardness, abrasion resistance, toughness, but also have excellent high temperature strength, thermal fatigue stability, thermal conductivity, upper hardenability for guaranteeing the whole cross section with consistent mechanical property.
PRODUCT PROFILE
Round bar / Wire rod (Diameter):  0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.  

TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineer.
- Email:
lh.steel@hotmail.com
 
 

Hot search:ASTM L3 /T61203

Previous page:ASTM L2 /T61202
Last page:ASTM L4 /T61204

Share to: