Technical specifications of DIN standards cold work alloy tool steels 1.2008 datasheet,DIN 1.2008 Chemical compositions, 1.2008 Mechanical properties from Steelmaking, ESR melted, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or rough turned machining. Technical specifications - ISO 4597 - 2001. We also possess the advanced precision machining equipments for catering for your different special requirements.
DIN 140Cr3 & 140Cr2 & W-Nr 1.2008 - DATA SHEET
Material category: Cold work alloy tool steel
TYPICAL APPLICATIONS
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / EAF + VD + LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the softened condition.
Final heat treatment - heat treatment / QT
MATERIAL SPECIFICATIONS
EN ISO 4957: 2000 , DIN 17350 (1980)
AVAILABLE SHAPES
Black bar /Flat bar /Square bar
Bright - peeled + polishing, centerless grinding
Forged - ring /tube /pipe casing /discs /shaft
CHEMICAL COMPOSITION (WEIGHT %) - DIN 140Cr3 / W-Nr 1.2008
C (％): 1.35 ~ 1.50
Si (％): 0.15 ~ 0.30
Mn (％): 0.25 ~ 0.40
P (％)≤: 0.035
S (％)≤: 0.035
Cr (％): 0.40 ~ 0.70
Mo (％): —
V (％): —
Si (％): 0.15 ~ 0.30
Mn (％): 0.25 ~ 0.40
P (％)≤: 0.035
S (％)≤: 0.035
Cr (％): 0.40 ~ 0.70
Mo (％): —
V (％): —
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1000～800
Annealing temperature /℃: 700～740
Hardness after annealing ≤HBW: 235
Quenching temperature /℃: 770～800
Cooling medium: OIL
Common tempering temperature /℃: 100～200
Hardness after tempering at temperature HRC|100℃: 66
Hardness after tempering at temperature HRC|200℃: 64
Hardness after tempering at temperature HRC|300℃: 60
Hardness after tempering at temperature HRC|400℃: --
Annealing temperature /℃: 700～740
Hardness after annealing ≤HBW: 235
Quenching temperature /℃: 770～800
Cooling medium: OIL
Common tempering temperature /℃: 100～200
Hardness after tempering at temperature HRC|100℃: 66
Hardness after tempering at temperature HRC|200℃: 64
Hardness after tempering at temperature HRC|300℃: 60
Hardness after tempering at temperature HRC|400℃: --
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to email or call our resident team of qualified production engineers. E-mail: sales@ccsteels.com
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 5.50mm to 600mm
Square bar / Flat bar: 30mm to 600mm
Plate / Sheet steel / Steel strip: 0.5mm to 600mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Hot search：1.2008
Total list
Monthly rank
- 30EN 28
- 1940CMD8
- 17115CrV3
- 15AISI M47 / ASTM M47
- 111.2333
- 11SS14 2140
- 955NCDV7
- 9SK85M / SK5M
- 8Carpenter 158
- 8SKS93