1.4905
2015-01-01 14:12:39 Origin： Remark：0 Click：
Description 1.4905 Inventory, Stocklist 1.4905 Round bar, Shaft 1.4905 From steelmaking, ESR, blooming, hot forging/rolling, heat treatment, straightened, 100% ultrasonic test, cold working, machined. We also possess advanced precision machining equipments for further processing.
TECHNICAL DATA SHEET - Heat Resisting Steel - DIN 1.4905
MATERIAL CATEGORY - Martensitic creep-resisting steels
FEATURES AND CLASSIFICATIONS
Heat-resistant steel means one type of steel possesses inoxidizability, enough high-temperature strength and excellent heat-resistant quality under high temperature. Heat resistant steel is divided into oxidation resistant steel and refractory steel according to its performance. Further into Austenitic heat-resistant steel, Martensitic heat-resistant steel, Ferritic heat-resistant steel and Pearlitic heat-resistant steel according to its normalizing.
Martensitic steel - Chromium content is 7～13%, which holds superior high temperature strength, inoxidizability and moisture corrosive resistance,but weldability is not good. 4Cr9Si2, 4Cr10Si2Mo are used to make the vent valves of internal combustion engine, also belong to Martensitic steel
Heat-resistant steel means one type of steel possesses inoxidizability, enough high-temperature strength and excellent heat-resistant quality under high temperature. Heat resistant steel is divided into oxidation resistant steel and refractory steel according to its performance. Further into Austenitic heat-resistant steel, Martensitic heat-resistant steel, Ferritic heat-resistant steel and Pearlitic heat-resistant steel according to its normalizing.
Martensitic steel - Chromium content is 7～13%, which holds superior high temperature strength, inoxidizability and moisture corrosive resistance,but weldability is not good. 4Cr9Si2, 4Cr10Si2Mo are used to make the vent valves of internal combustion engine, also belong to Martensitic steel
MATERIAL SPECIFICATIONS - DIN 17442,17744, DIN EN 10302, 10095, EN 10088-1 (2005)
CHEMICAL COMPOSITION (Mass weight - %)
C (％): 0.08 ~ 0.13
Si (％): 0.10 ~ 0.50
Mn (％): 0.30 ~ 0.60
C (％): 0.08 ~ 0.13
Si (％): 0.10 ~ 0.50
Mn (％): 0.30 ~ 0.60
P (％)≤: 0.020
S (％)≤: 0.010
Cr (％): 8.50 ~ 9.50
Ni (％): 0.10 ~ 0.40
S (％)≤: 0.010
Cr (％): 8.50 ~ 9.50
Ni (％): 0.10 ~ 0.40
Mo (%): 0.90 ~ 1.10
W (%): 0.90 ~ 1.10
Other (％): N 0.05 ~ 0.09, Nb 0.06 ~ 0.10, V 0.18 ~ 0.25, Al ≤0.040, B 0.0005~0.005
Other (％): N 0.05 ~ 0.09, Nb 0.06 ~ 0.10, V 0.18 ~ 0.25, Al ≤0.040, B 0.0005~0.005
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Heat treatment: -
Heat treatment: -
Condition: annealed
Tensile strength, σb/MPa: 950 min.
Tensile strength, σb/MPa: 950 min.
Yield strength, σs≥/MPa: 785 min.
Elongation, δ5 ≥(％): 15.0
Elongation, δ5 ≥(％): 15.0
APPLICATION FIELD
Heat-resistant steel is widely used in the field of manufacturing the boiler, steam turbine, motive power machine, industrial furnace, and other mechanical parts of aviation, petrochemical engineering operating at high temperature. Those parts must hold the features: high temperature strength, resistance to high temperature oxide etch, enough toughness, excellent machinability, weldability, structure stability based on different usages.
Heat-resistant steel is widely used in the field of manufacturing the boiler, steam turbine, motive power machine, industrial furnace, and other mechanical parts of aviation, petrochemical engineering operating at high temperature. Those parts must hold the features: high temperature strength, resistance to high temperature oxide etch, enough toughness, excellent machinability, weldability, structure stability based on different usages.
MANUFACTURING TECHNOLOGY - SMELTING
Heat resistant steel is generally smelt in electric arc furnace or induction furnace. For higher quality,it should be smelt via technology of vacuum refining and external refining.
Heat resistant steel is generally smelt in electric arc furnace or induction furnace. For higher quality,it should be smelt via technology of vacuum refining and external refining.
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 400mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 400mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 300mm X W40 - 1200mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
HEAT TREATMENT PRACTICE
Pearlitic refractory steels use normalizing or hardening and tempering.
Martensitic heat resistant steels adopt hardening and tempering to stabilize the structure for excellent composite mechanical properties and high temperature strength.
Pearlitic refractory steels use normalizing or hardening and tempering.
Martensitic heat resistant steels adopt hardening and tempering to stabilize the structure for excellent composite mechanical properties and high temperature strength.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers.Email: sales@ccsteels.com.
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers.Email: sales@ccsteels.com.
Hot search：1.4905
Previous page：X11CrMoWVNb9-1-1
Last page：X6CrNi23-13