TECHNICAL SPECIFICATION DATASHEET - DIN X120Mn13
Si (％): ≤ 0.50
Mn (％): 11.5 ~ 13.5
P (％)≤: 0.060
S (％)≤: 0.030
Cr (％): ≤ 0.50
Ni (％): -
Mo (％): -
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Yield strength, σ0.2 ≥/MPa: 295
Elongation, δ≥(％): 25.0
Impact strength, Akv ≥/J: -
The alloy is usually produced by AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Round bar / Wire rod (Diameter): 5.5mm to 400mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.