FV535, a Martensitic Chromium - Cobalt - Nickel - Molybdenum Base Steel, FV535 Round bar, flat bar and forgings Steelmaking, ESR, Hot forging & rolling, heat treated, cold machined.
TECHNICAL DATA SHEET - Grade FV535
MATERIAL CATEGORY - Martensitic creep-resisting steels
HS Code for Customs - 72221100 / 72221900 / 72223000
Stocklist on hand - Round bar diam.60mm
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): 0.05 ~ 0.12
Silicon, Si (％): 0.10 ~ 0.80
Manganese, Mn (％): 0.30 ~ 1.30
Phosphorus, P (％)≤: 0.025
Sulfur, S (％)≤: 0.015
Chromium, Cr (％): 9.80 ~ 11.2
Nickel, Ni (％): 0.20 ~ 1.20
Molybdenum, Mo (％): 0.50 ~ 1.00
Aluminum, Al (%): -
Vanadium, V (%): 0.10 ~ 0.40
Titanium, Ti (%): -
Tungsten, W (%): ≤ 0.70
Niobium, Nb (%): 0.20 ~ 0.50
Cobalt, Co (%): 5.00 ~ 7.00
Boron, B (%): 0.005 ~ 0.015
Other (％): N ≤0.035
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: heat treatment
Tensile strength, σb/MPa: 980 ~ 1130
Yield strength, σs≥/MPa: 835 min.
Elongation, δ5≥(％): 15.0
Non-scale temperature in Air: 700℃
MANUFACTURING TECHNOLOGY - SMELTING
Heat resistant steel is generally smelt in electric arc furnace or induction furnace. For higher quality,it should be smelt via technology of vacuum refining and external refining.
PROFILE AND DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 ~ 400mm X W10 ~ 1000mm X L1000 ~ 5000mm
Sheet steel via cold rolled: T1.0 - 6mm X W6 ~ 1000mm X L1000 ~ 2000mm
Steel strip via cold rolled: T0.5 ~ 3mm X W5 ~ 200mm X L (or in coil form)
Forging piece: stepped shafts, andother different shapes based on OEM.