AMS 6419
2025-12-15 11:40:00 Origin： Remark：0 Click：
Description AMS 6419 Bars, Strip AMS 6419 Inventory, Ex-stock AMS 6419 Ring forging, Wire rod, 300M sheet - Steelmaking, ESR, Blooming, Hot forging, Hot rolling, Heat treated
TECHNICAL DATA SHEET - AMS 6419
Official test report: issued by TUV - SGS - BV
Technical specifications: EN 10084 (1998), DIN 17210 (1986)
Melting process: VIM + VAR or consumable electrode remelted
Melting process: VIM + VAR or consumable electrode remelted
Typical chemical compositions (mass weight %)
Carbon, C (％): 0.38 ~ 0.46
Silicon, Si (％): 1.45 ~ 1.80
Manganese, Mn (％): 0.60 ~ 0.90
Phosphorus, P (％): ≤ 0.010
Sulfur, S (％): ≤ 0.010
Chromium, Cr (％): 0.70 ~ 0.95
Nickel, Ni (％): 1.65 ~ 2.00
Molybdenum, Mo (％): 0.30 ~ 0.65
Vanadium, V (%): 0.05 ~ 0.10
TYPICAL MECHANICAL PROPERTIES
Form: Bar, plate, sheet, forging
Condition: normalized, hardened and double tempered
Tensile strength, σb / MPa: 1930 min.
Yield strength, σ0.2 / MPa: 1580 min.
Elongation, δ5 (％): 7 min.
Reduction of area, ф (％): -
Hardness (HBW): -
APPLICATION FIELD
Aircraft landing gear.
High strength bolts.
Airframe parts.
Driveshafts.
Carbon, C (％): 0.38 ~ 0.46
Silicon, Si (％): 1.45 ~ 1.80
Manganese, Mn (％): 0.60 ~ 0.90
Phosphorus, P (％): ≤ 0.010
Sulfur, S (％): ≤ 0.010
Chromium, Cr (％): 0.70 ~ 0.95
Nickel, Ni (％): 1.65 ~ 2.00
Molybdenum, Mo (％): 0.30 ~ 0.65
Vanadium, V (%): 0.05 ~ 0.10
TYPICAL MECHANICAL PROPERTIES
Form: Bar, plate, sheet, forging
Condition: normalized, hardened and double tempered
Tensile strength, σb / MPa: 1930 min.
Yield strength, σ0.2 / MPa: 1580 min.
Elongation, δ5 (％): 7 min.
Reduction of area, ф (％): -
Hardness (HBW): -
APPLICATION FIELD
Aircraft landing gear.
High strength bolts.
Airframe parts.
Driveshafts.
PRODUCT PROFILE & AVAILABLE SIZE
Round bar / rod / disc (diameter): 6.0 to 600 mm
Square bar / flat bar: 10 to 800 mm
Length: random length or based on the customer's special requirement.
The alloy is usually produced by VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Round bar / rod / disc (diameter): 6.0 to 600 mm
Square bar / flat bar: 10 to 800 mm
Length: random length or based on the customer's special requirement.
The alloy is usually produced by VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL(sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry. pleased to EMAIL(sales@ccsteels.com) our resident team of qualified production engineers.
Jiangyou Longhai Special Steel Co.,Ltd
ISO 9001-2015 Certified
Raw material stock available
Custom 450 / XM-25 / S45000, 403 ESR, AISI 616 / 422 ESR, B50A365 / 403Cb+
17-4PH / 630, M-152 / 1.4938 / S151 / S159, S111, FV520B / S143 / 1.4594
X8CrMnN18-18, X40MnCrN19, X40MnCr18, X55MnCrN18-4
13Х11Н2B2MФ / AE961W, 11Х11Н2B2MФ / 16Х11Н2B2MФ
15-5PH / XM-12 (S15500), A-286 AISI 660 / S66286
10705BU, 10705MBU, 10705AJ
Total list
Monthly rank
- 18S135
- 1611SMnPb30
- 15NF 20NC11
- 14EN35B
- 141.7380
- 14SCr435
- 13ASTM 1526/G15260
- 13635H15 / 635M15 / En351
- 131.7005
- 13AISI 8645H