ASTM A182 type F9
2019-09-19 16:03:28 Origin： Remark：0 Click：
ASTM A182 Grade F9 Round bar, Plate, Forgings ASTM A182 Grade F9 property from Steelmaking, ESR melted, Hot forging / rolling, Heat treatment
TECHNICAL DATA SHEET - ASTM A182 Grade F9
MATERIAL TECHNICAL STANDARDS: ASTM A182 - 2018
MATERIAL TYPE: 9Cr- 1.0Mo Alloy steel
CHEMICAL COMPOSITION (mass weight -%)
Carbon, C (％): ≤ 0.15
Manganese, Mn (％): 0.30 ~ 0.60
Silicon, Si (％): 0.50 ~ 1.00
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (%): 8.00 ~ 10.0
Molybdenum, Mo (%): 0.90 ~ 1.10
Nickel, Ni (%): -
Niobium, Nb (%): -
Titanium, Ti (%): -
TYPICAL MECHANICAL PROPERTIES
Tensile strength, Rm ≥ MPa: 585
Yield strength, Rp0.2 / MPa: 380
Elongation, A5 ≥ (％): 22.0
Reduction of area, Z ≥ (％): 40.0
Manganese, Mn (％): 0.30 ~ 0.60
Silicon, Si (％): 0.50 ~ 1.00
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (%): 8.00 ~ 10.0
Molybdenum, Mo (%): 0.90 ~ 1.10
Nickel, Ni (%): -
Niobium, Nb (%): -
Titanium, Ti (%): -
TYPICAL MECHANICAL PROPERTIES
Tensile strength, Rm ≥ MPa: 585
Yield strength, Rp0.2 / MPa: 380
Elongation, A5 ≥ (％): 22.0
Reduction of area, Z ≥ (％): 40.0
Hardness via heat treatment /HBW: 179 ~ 217
Hardness via heat treatment /HBW: 179 ~ 217
HEAT TREATMENT PRACTICE
Condition: annealed 955 Deg.
Cooling medium: furnace cool
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Disc (diameter): 5.5mm to 650mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 400mm X W200- 1200mm X L1000-5000mm
Forging piece: stepped shaft, and other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical inquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hardness via heat treatment /HBW: 179 ~ 217
HEAT TREATMENT PRACTICE
Condition: annealed 955 Deg.
Cooling medium: furnace cool
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Disc (diameter): 5.5mm to 650mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 400mm X W200- 1200mm X L1000-5000mm
Forging piece: stepped shaft, and other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical inquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Total list
Monthly rank
- 21AISI/SAE 6135
- 1852CrMoV4
- 17X46Cr13
- 1638NiCrMo4
- 16ASTM A182 type F11 Class 1
- 14805A22
- 14AMS 6320
- 141.0460
- 1425MNDC6
- 1426NiCrMoV14-5