ASTM A514 Gr.E
2020-12-14 11:03:39 Origin： Remark：0 Click：
Specifications ASTM A514 Gr.E Round bar, Flat bar, Plate and Forgings ASTM A514 Gr.E Steelmelting (ESR refined), Hot rolling, Heat treatment
TECHNICAL DATA SHEET - ASTM A514 Grade E
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (％): 0.12 ~ 0.20
Carbon, C (％): 0.12 ~ 0.20
Silicon, Si (％): 0.20 ~ 0.40
Manganese, Mn (％): 0.40 ~ 0.70
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.025
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.025
Chromium, Cr (%): 1.40 ~ 2.00
Molybdenum, Mo (%): 0.40 ~ 0.60
Titanium, Ti (%): 0.01 ~ 0.10
Boron, B (%): 0.001 ~ 0.005
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, Rm / MPa: 760
Yield strength, Rp0.2 / MPa: 690
Elongation, A5 (％): 18.0
Reduction of area, Z (％): -
Elongation, A5 (％): 18.0
Reduction of area, Z (％): -
Hardness (HBW): 295 max.
MELTING PROCESS
This alloy is generally smelt in Non-vacuum furnace + ESR, Electric Arc Furnace (EAF).
For a purpose of superior quality, it should be smelt via technology of Electroslag remelting or vacuum refining or by agreement.
This alloy is generally smelt in Non-vacuum furnace + ESR, Electric Arc Furnace (EAF).
For a purpose of superior quality, it should be smelt via technology of Electroslag remelting or vacuum refining or by agreement.
PRODUCT PROFILE AND DIMENSIONS
Round bar & Disc (diameter): 5.5 to 800mm
Steel strip: THK0.15 ~ 2.50 X W8.0 ~ 550mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL(sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry, pleased to EMAIL(sales@ccsteels.com) our resident team of qualified production engineers.
Previous page：A514 GRADE A
Last page：AMS 5525
Total list
Monthly rank
- 6124CrMo5
- 5542Cr4Mo2
- 52EN 14B
- 4838NCD4
- 47EN 38
- 4534CrNiMo4
- 44ASTM A739 Gr. B11
- 43EN 355
- 42X20CrMoV12-1
- 4240Cr4