DTD 2 / MSRR 6004
2024-03-30 09:07:26 Origin： Remark：0 Click：
DTD Specifications Structural Alloy Steel for Aviation DTD 2 & MSRR 6004 Round bar, Flat bar, Forgings used for larger preshaped components in turbine and generator installations, shafts and discs.
MATERIAL TECHNICAL DATASHEET - DTD 2 & MSRR 6004
Material Category: Hardened and tempered steel
Material Specification - DTD Alloy Steel Series or by agreement
Melting process method - EF + Consumable electrode remelted
HS code for Customs: 7228 4000 / 7228 5000
Main Chemical composition (mass weight - %)
Carbon, C (％): 0.10 ~ 0.15
Silicon, Si (％): 0.10 ~ 0.35
Manganese, Mn (％): 0.35 ~ 0.60
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 0.20 ~ 0.30
Molybdenum, Mo (％): -
Nickel, Ni (％): 2.75 ~ 3.25
Ferrum, Fe (％): balance.
Material Category: Hardened and tempered steel
Material Specification - DTD Alloy Steel Series or by agreement
Melting process method - EF + Consumable electrode remelted
HS code for Customs: 7228 4000 / 7228 5000
Main Chemical composition (mass weight - %)
Carbon, C (％): 0.10 ~ 0.15
Silicon, Si (％): 0.10 ~ 0.35
Manganese, Mn (％): 0.35 ~ 0.60
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 0.20 ~ 0.30
Molybdenum, Mo (％): -
Nickel, Ni (％): 2.75 ~ 3.25
Ferrum, Fe (％): balance.
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Hot working temperature /℃: 1050 ~ 850
Hardness after annealing ≤HBS: 239
Tensile strength, |σb≥/MPa: 850
Yield strength, |σs≥/MPa: 310
Elongation, |δ5≥/(%): 15.0
Reduction of area, |ψ≥/(%): -
Hot working temperature /℃: 1050 ~ 850
Hardness after annealing ≤HBS: 239
Tensile strength, |σb≥/MPa: 850
Yield strength, |σs≥/MPa: 310
Elongation, |δ5≥/(%): 15.0
Reduction of area, |ψ≥/(%): -
PRODUCT DESCRIPTION
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF / VD / LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied in the annealed, peeled bright condition.
Final heat treatment - Quenched and tempered.
PRODUCT PROFILE & DIMENSIONS
Round bar / Disc (diameter): 5.5mm to 850mm
Square bar / Flat bar: 6mm to 650mm
Plate / Steel strip: 1.0mm to 200mm
Steel sheet: thickness 1.0 ~ 4.0mm, width 10 ~ 1000mm X length 1000/2000mm - Standard size
Length: random length or based on the customer's special requirement
Forged steel shape: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
If you meet further on any technical enquiry. pleased to email or call our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Previous page：21CrMoVA
Last page：X14CrMoVNbN10-1
Total list
Monthly rank
- 6124CrMo5
- 5542Cr4Mo2
- 52EN 14B
- 4838NCD4
- 47EN 38
- 4534CrNiMo4
- 44ASTM A739 Gr. B11
- 43EN 355
- 42X20CrMoV12-1
- 4240Cr4