Material Specifications ASTM A565 Martensitic Alloy Steel S64152 Round bar, Flat bar, Plate, Hexagon bar, Hot forging & hot rolling, Heat treatment, Cold working.
MARTENSITIC STEEL DATA SHEET - UNS S64152
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
STOCK AVAILABLE - Round bar diam. 50 ~ 230mm
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.08 ~ 0.15
Silicon, Si (％): ≤ 0.35
Manganese, Mn (％): 0.50 ~ 0.90
PHosphorus, P (％)≤: 0.025
Sulfur, S (％)≤: 0.025
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 2.00 ~ 3.00
Molybdenum, Mo (％): 1.50 ~ 2.00
Silicon, Si (％): ≤ 0.35
Manganese, Mn (％): 0.50 ~ 0.90
PHosphorus, P (％)≤: 0.025
Sulfur, S (％)≤: 0.025
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 2.00 ~ 3.00
Molybdenum, Mo (％): 1.50 ~ 2.00
Vanadium, V (％): 0.25 ~ 0.40
Nitrogen, N (%): 0.01 ~ 0.05
TYPICAL MECHANICAL PROPERTIES
Condition of heat treatment: annealing
Tensile Strength, σb/MPa: 1000
Yield Strength, σ0.2/MPa: 795
Yield Strength, σ0.2/MPa: 795
Elongation, δ(％): 15.0
Reducion of area, ф (％): 30.0
Hardness | HRB: ≤311
Reducion of area, ф (％): 30.0
Hardness | HRB: ≤311
condition of heat treatment: HT:955℃~1022℃ air/oil cooling, >=565℃ X 2h tempering
Tensile strength, σb/MPa: 1000
Yield strength, σ0.2/MPa: 795
Yield strength, σ0.2/MPa: 795
Elongation, δ (％): 13.0
Reduction of area, ф (％): 35.0
Hardness | HBW: 302 ~ 352
Reduction of area, ф (％): 35.0
Hardness | HBW: 302 ~ 352
PRODUCT DESCRIPTION
The alloy is usually produced by BEF + AOD / EAF followed by electroslag refining (ESR or VAR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the annealed condition.
Final heat treatment - Quenched and tempered, + SRA
The alloy is usually produced by BEF + AOD / EAF followed by electroslag refining (ESR or VAR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the annealed condition.
Final heat treatment - Quenched and tempered, + SRA
FORMS AND DIMENSIONS
Round bar & Disc: diam. 5.5 ~ 800mm
Heavy/middle plate via hot forged / rolled: T60 - 350mm X W100 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T1.0 - 4mm X W10 - 300mm X L1000 - 2000mm
Steel strip via cold rolled: T0.5 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Sheet steel via cold rolled: T1.0 - 4mm X W10 - 300mm X L1000 - 2000mm
Steel strip via cold rolled: T0.5 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to Email (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry, pleased to Email (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：S64152
Previous page：SKD12 / 1.2363 / A2
Last page：SKD4
Total list
Monthly rank
- 50FSX-414
- 16Aquamet 22
- 1510705BU
- 15AMS 5221
- 13Carpenter 20 Mo 4
- 12X12CrNiMoV12-2
- 11Inconel 610
- 10AMS 5354
- 9Incoloy 840
- 8Aquamet 17