12Cr - 3.0Ni -2.0Mo martensitic stainless steel Jethete M152 data sheet, round bar, flat bar jethete M152 properties from steel making, ESR melted, hot bloomed, forged, rolled, heat treated
MATERIAL DATA SHEET - Jethete M152
Typical chemical compositions (mass weight - %)
Carbon, C (％): 0.08 ~ 0.13
Silicon, Si (％): ≤ 0.35
Manganese, Mn (％): 0.50 ~ 0.90
Phosphorus, P (％): ≤ 0.030
Sulfur, S (％): ≤ 0.025
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 2.00 ~ 3.00
Molybdenum, Mo (％): 1.50 ~ 2.00
Manganese, Mn (％): 0.50 ~ 0.90
Phosphorus, P (％): ≤ 0.030
Sulfur, S (％): ≤ 0.025
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 2.00 ~ 3.00
Molybdenum, Mo (％): 1.50 ~ 2.00
Nitrogen, N (%): 0.01 ~ 0.05
Vanadium, V (%): 0.25 ~ 0.40
Copper, Cu (%): ≤ 0.50
MECHANICAL PROPERTIES UNDER ROOM TEMP
Condition, bar: 1020 hardening treated
Tensile strength, σb ≥ MPa: 930 ~ 1130
Yield strength, σ0.2 ≥ MPa: 780
Elongation, δ5 ≥ : 14.0
Elongation, δ5 ≥ : 14.0
Reduction of area ф ≥ : -
Hardness, HB: 280 ~ 331
PROFILES AND DIMENSIONS
Round bar, rod, disc (diameter): 6.0 to 900 mm
Square bar, flat bar: 10 to 500 mm
Heavy/middle plate via hot rolled: T6 ~ 400 x W20 ~ 1000 x L mm
Forging piece: stepped shafts, other different shapes based on OEM.
Square bar, flat bar: 10 to 500 mm
Heavy/middle plate via hot rolled: T6 ~ 400 x W20 ~ 1000 x L mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to Email our resident team of qualified production engineers, Email: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to Email our resident team of qualified production engineers, Email: sales@ccsteels.com
Previous page：M-152 / S64152 / 1.4938 Forgings
Last page：27NiCrMoV11-6