Duratherm 600
2026-05-08 06:50:00 Origin： Remark：0 Click：
Specifications Duratherm 600 technical data sheet, Duratherm 600 round bar, wire rod, plate, strip, ESR melted, hot forged & rolled, cold rolled, heat treated
TECHNICAL DATA SHEET - Duratherm 600
Official test report: issued by TUV - SGS - CNAS
Material category: Cr - Ni- Mo - Co - W Series alloy
Typical chemical compositions (mass weight - %)
Carbon, C (％): ≤ 0.05
Silicon, Si (％): 0.20 ~ 0.60
Manganese, Mn (％): 0.40 ~ 1.10
Phosphrous, P (％): ≤ 0.030
Carbon, C (％): ≤ 0.05
Silicon, Si (％): 0.20 ~ 0.60
Manganese, Mn (％): 0.40 ~ 1.10
Phosphrous, P (％): ≤ 0.030
Sulfur, S (％): ≤ 0.020
Chromium, Cr (％): 11.7 ~ 12.3
Chromium, Cr (％): 11.7 ~ 12.3
Nickel, Ni (％): balance
Molybdenum, Mo (％): 3.70 ~ 4.30
Cobalt, Co (%): 41.0 ~ 42.0
Cobalt, Co (%): 41.0 ~ 42.0
Tungsten, W (%): 3.60 ~ 4.20
Aluminum, Al (%): 0.60 ~ 0.80
Aluminum, Al (%): 0.60 ~ 0.80
Copper, Cu (%): ≤ 0.30
Titanium, Ti (%): 1.80 ~ 2.20
Titanium, Ti (%): 1.80 ~ 2.20
Ferrum, Fe (%): 8.50 ~ 8.90
Niobium, Nb (%): ≤ 0.10
Beryllium, Be (%): ≤ 0.05
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: Solution + Aged treated (750 Deg.)
Tensile strength, σb/≥ MPa: 850 ~ 1100
Yield strength, σ0.2/≥ MPa: 380 ~ 650
Elongation, δ ≥(％): 20.0
Reduction of area, ф ≥ (％): -
Hardness | HBW: 210 ~ 310
Reduction of area, ф ≥ (％): -
Hardness | HBW: 210 ~ 310
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged
PROFILES AND DIMENSIONS
Round bar (diameter): 5.5mm to 450 mm
Square bar / flat bar: 10 to 400 mm
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged
PROFILES AND DIMENSIONS
Round bar (diameter): 5.5mm to 450 mm
Square bar / flat bar: 10 to 400 mm
Wire rod (Diameter): 0.20 to 13mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our qualified production engineers. -You can reach our sales dept via E-mail: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our qualified production engineers. -You can reach our sales dept via E-mail: sales@ccsteels.com
Total list
Monthly rank
- 20N06617
- 18ASTM B805 N07773
- 15X15CrMo12-1
- 15X20CrMoV12-1
- 14K94100
- 132.4632
- 13Nimonic 90
- 131.4971
- 13AMS 5510
- 13X8CrNiMoNb16-16