XM-25
2020-04-16 14:44:25 Origin： Remark：0 Click：
Specifications XM-25 Ex-stock, XM-25 Chemical, XM-25 Suppliers properties from Steelmaking, ESR melted, Blooming, Hot forging Hot rolling, Heat treatment, Straightening, Ultrasonic test,Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
ALLOY STEEL TECHNICAL DATA SHEET - Grade XM-25
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL TYPE: Custom 450 (XM-25) stainless has very good corrosion resistance with moderate strength. A single-step aging treatment develops higher strength with good ductility and toughness.
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.05
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.030
C (％): ≤ 0.05
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.030
S (％)≤: 0.025
Cr (％): 14.0 ~ 16.0
Cr (％): 14.0 ~ 16.0
Ni (％): 5.00 ~ 7.00
Mo (％): 0.50 ~ 1.00
Co (%): -
Co (%): -
W (%): -
Al (%): -
Al (%): -
Cu (%): 1.25 ~ 1.75
Ti (%): -
Ti (%): -
Nb (%): 8 X C Min.
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Tensile strength, σb/≥ MPa: 895
Yield strength, σ0.2/≥ MPa: 655
Elongation, δ ≥(％): 10.0
Reduction of area, ф ≥ (％): 40.0
Hardness | HBW: HRC 32 min.
Elongation, δ ≥(％): 10.0
Reduction of area, ф ≥ (％): 40.0
Hardness | HBW: HRC 32 min.
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
FORMS AND SHAPES
Round bar (Diameter): 5.5mm to 650mm
Square bar / Flat bar: 3mm to 450mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
FORMS AND SHAPES
Round bar (Diameter): 5.5mm to 650mm
Square bar / Flat bar: 3mm to 450mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers.
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers.
Hot search：XM-25
Total list
Monthly rank
- 50FSX-414
- 16Aquamet 22
- 1510705BU
- 15AMS 5221
- 13Carpenter 20 Mo 4
- 12X12CrNiMoV12-2
- 11Inconel 610
- 10AMS 5354
- 9Incoloy 840
- 8Aquamet 17